Park Electrochemical Nelcote® E-761 Epoxy Prepreg, 3K 8HS Carbon Reinforced

Category	Polymer , Thermoset , Epoxy
Manufacturer	Park Electrochemical Corp.
Trade Name	Nelcote®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Park Electrochemical Nelcote® E-761 Epoxy Prepreg, 3K 8HS Carbon Reinforced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Nelcote® E-761 is a versatile self-adhesive epoxy matrix for use in aerospace and commercial application where ease of processing and cost are key considerations.Key Features and Benefits:Controlled flow for ease of processingSelf adhesive for honeycomb or foam sandwich laminates without the use of film adhesiveFlexible cure temperature 180°F to 250°FGood electrical propertiesFlame and fire retardant per FAR 25.853Wet service temperatures up to 160°FApplications/Qualifications:RadomesAircraft InteriorsSecondary Aircraft StructuresSandwich PanelsMRI ResonatorsWidely specified on commercial and military aircraft programsInformation provided by Park Electrochemical Corp.

Physical Properties	Metric	English	Comments
Volatiles	<= 2.0 % @Temperature 135 °C	<= 2.0 % @Temperature 275 °F	8 min
Thickness	356 microns	14.0 mil	Per Ply

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	586 MPa @Temperature 21.1 °C	85000 psi @Temperature 70.0 °F	0° Direction, Dry; ASTM D638
Tensile Modulus	55.2 GPa @Temperature 21.1 °C	8000 ksi @Temperature 70.0 °F	0° Direction, Dry; ASTM D638
Flexural Strength	42.7 MPa @Temperature 21.1 °C	6200 psi @Temperature 70.0 °F	Dry; ASTM D790
Flexural Modulus	54.5 GPa @Temperature 21.1 °C	7900 ksi @Temperature 70.0 °F	Dry; ASTM D790
Compressive Strength	510 MPa @Temperature 21.1 °C	74000 psi @Temperature 70.0 °F	Dry; ASTM D695
Compressive Modulus	53.1 GPa @Temperature 21.1 °C	7700 ksi @Temperature 70.0 °F	Dry; ASTM D695
Shear Strength	54.5 MPa @Temperature 21.1 °C	7900 psi @Temperature 70.0 °F	Short-Beam, Dry; ASTM D2344

Thermal Properties	Metric	English	Comments
Glass Transition Temp, Tg	115 °C	239 °F	Dry; DMA

Processing Properties	Metric	English	Comments
Gel Time	6.25 min	6.25 min
Shelf Life	12.0 Month @Temperature -17.8 °C	12.0 Month @Temperature 0.000 °F

Descriptive Properties	Value	Comments
Fabric Area Weight (g/m²)	369.9
Prepreg Resin Content (%)	42
Resin Flow (%)	12	275°F, 50psi