PTS PCA-3015 Low Temperature Impact PC/PBT Alloy
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | Polymer Technology & Services, LLC (PTS) |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PTS PCA-3015 Low Temperature Impact PC/PBT Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in³ | ASTM D792 |
| Water Absorption | 0.030 % | 0.030 % | 24 hours at 73°F; ASTM D570 |
| Linear Mold Shrinkage | 0.0075 cm/cm | 0.0075 in/in | ASTM D955 |
| Melt Flow | 2.0 g/10 min @Load 5.00 kg, Temperature 250 °C |
2.0 g/10 min @Load 11.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 51.0 MPa @Thickness 3.17 mm |
7400 psi @Thickness 0.125 in |
ASTM D638 |
| Elongation at Break | 150 % @Thickness 3.17 mm |
150 % @Thickness 0.125 in |
ASTM D638 |
| Flexural Yield Strength | 85.5 MPa @Thickness 3.17 mm |
12400 psi @Thickness 0.125 in |
ASTM D790 |
| Flexural Modulus | 1.86 GPa @Thickness 3.17 mm |
270 ksi @Thickness 0.125 in |
ASTM D790 |
| Izod Impact, Notched | 8.01 J/cm @Thickness 3.17 mm |
15.0 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 116 °C | 241 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C | 205 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 232 - 243 °C | 450 - 470 °F | |
| Middle Barrel Temperature | 238 - 254 °C | 460 - 490 °F | |
| Front Barrel Temperature | 246 - 268 °C | 475 - 515 °F | |
| Nozzle Temperature | 246 - 266 °C | 475 - 510 °F | |
| Melt Temperature | 243 - 279 °C | 470 - 535 °F | |
| Mold Temperature | 65.6 - 82.2 °C | 150 - 180 °F | |
| Drying Temperature | 110 °C | 230 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Back Pressure | 0.000 - 3.45 MPa | 0.000 - 500 psi | |
| Shot Size | 50 - 80 % | 50 - 80 % | |
| Screw Speed | 20 - 60 rpm | 20 - 60 rpm |
Users viewing this material also viewed the following:
- RheTech Products RCC220-01 20% Calcium Carbonate Reinforced Polypropylene Copolymer, Black, Recycled Content
- Omni Plastics OmniTuff™ CPP TF30 Copolymer Polypropylene Talc Filled
- MarkeTech Repton 136 Aluminum Oxide
- Lanxess Durethan® DP 1852/30 000000 Nylon 6, 30% Glass Fiber
- SABIC Innovative Plastics LNP LUBRICOMP RBL36L PA 66
- Polyplastics Duranex® 2002U Polybutylene Terephthalate (PBT), Weather resistance
- Wall Colmonoy COLMONOY® 83 PTA - Nickel-Chromium-Boron Matrix Alloy With Tungsten Carbide
- Dow Corning XIAMETER® PMCPMEM-0008 Emulsion
- DuPont Performance Polymers Delrin® 150 NC010 Acetal (POM) (Unverified Data**)
- Asahi Glass F-Clean® Film for Greenhouses
Copyright © lookpolymers.com All Rights Reserved