PCC-Advanced Forming Technology 63% AlSiC Metal Matrix Composite

Category Metal , Metal Matrix Composite
Manufacturer PCC-Advanced Forming Technology
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PCC-Advanced Forming Technology 63% AlSiC Metal Matrix Composite.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
AlSiC metal matrix composites are formed by pressure infiltrating molten aluminum into silicon carbide preforms. This method of casting is typically used in applications where solution requirements include high strength, lightweight, custom CTE and high thermal conductivity. PCC offers AlSiC with a composition varying between 30% to 74% silicon carbide by volume, depending on the application. This flexible material system allows PCC Composites to produce a part that is tailored to a customer's exact solution requirements.Infomation provided by PCC-Advanced Forming Technology.
Physical Properties Metric English Comments
Density 3.01 g/cc
0.109 lb/in³
Mechanical Properties Metric English Comments
Hardness, Rockwell B 88
88
Tensile Strength, Ultimate 253 MPa
36700 psi
Modulus of Elasticity 220 GPa
31900 ksi
Young's Modulus
Flexural Strength 369 MPa
53500 psi
Thermal Properties Metric English Comments
CTE, linear 8.00 µm/m-°C

@Temperature 20.0 - 50.0 °C
4.44 µin/in-°F

@Temperature 68.0 - 122 °F
8.20 µm/m-°C

@Temperature 20.0 - 150 °C
4.56 µin/in-°F

@Temperature 68.0 - 302 °F
Thermal Conductivity 175 W/m-K
1210 BTU-in/hr-ft²-°F
Melting Point 557 - 613 °C
1030 - 1140 °F
Solidus 557 °C
1030 °F
Liquidus 613 °C
1140 °F
Maximum Service Temperature, Air 420 °C
788 °F
Maximum exposure temp.