- Owens Corning Glass Fiber Reinforced Polyphenylene Oxide (PPO), 20 wt.% glass
Owens Corning Glass Fiber Reinforced Polyphenylene Oxide (PPO), 20 wt.% glass
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, 20% Glass Filled |
| Manufacturer | Owens Corning |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Owens Corning Glass Fiber Reinforced Polyphenylene Oxide (PPO), 20 wt.% glass.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyphenylene Oxide provides excellent resistance to aqueous media. It is softened by aromatic hydrocarbons. Data provided by the manufacturer, Owens Corning.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in³ | ASTM D792 |
| Water Absorption | 0.24 % | 0.24 % | 24 hrs.; ASTM D570 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 107 | 107 | ASTM D785 |
| Tensile Strength, Ultimate | 100 MPa | 14500 psi | ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 |
| Modulus of Elasticity | 6.30 GPa | 914 ksi | ASTM D638 |
| Flexural Strength | 128 MPa | 18600 psi | ASTM D790 |
| Flexural Modulus | 5.20 GPa | 754 ksi | ASTM D790 |
| Compressive Strength | 121 MPa | 17500 psi | ASTM D695 |
| Izod Impact, Notched | 0.960 J/cm | 1.80 ft-lb/in |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.2 @Frequency 60 Hz |
3.2 @Frequency 60 Hz |
ASTM D150 |
| Dielectric Strength | 19.7 kV/mm | 500 kV/in | ASTM D149 |
| Arc Resistance | 70 sec | 70 sec | ASTM D495 |
Users viewing this material also viewed the following:
- Solvay Engineered Polymers INDURE™ E1600 TPO (discontinued **)
- Lushan EF-3 Adhesive Resin for Coextruded Multi-layer Barrier Packaging Film
- Schott N-KZFS11 Glass
- Dow Corning SE 1816 CV KIT
- Chosun Refractories SFC-UL90S High-Alumina Castable
- Aclo Accucomp Polypropylene CPO402V Automotive Approved Copolymer Extrusion Grade
- AKG Polymers Vision PP PPC BL10004 Polypropylene Copolymer Compound
- Akzo Nobel Trigonox® D-E50 Polymerization Initiator
- PolyOne Synprene® RT-3955 Thermoplastic Elastomer - SBC (discontinued **)
Copyright © lookpolymers.com All Rights Reserved