Ovation Polymers OPTRENE 20GF Polypropylene, 20% Glass Reinforced

Category	Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer	Ovation Polymers
Trade Name	Optrene
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Ovation Polymers OPTRENE 20GF Polypropylene, 20% Glass Reinforced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Properties of chemically coupled glass reinforced (20%) polypropylene with high strength and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are prepared according to ASTM standards. Variations within normal tolerances are possible for various types of colors and functional properties like UV resistance.Information provided by Ovation Polymers

Physical Properties	Metric	English	Comments
Specific Gravity	1.033 g/cc	1.033 g/cc	ASTM D792
Linear Mold Shrinkage	0.0024 - 0.0030 cm/cm @Thickness 3.17 mm	0.0024 - 0.0030 in/in @Thickness 0.125 in
Linear Mold Shrinkage, Transverse	0.0080 - 0.012 cm/cm @Thickness 3.17 mm	0.0080 - 0.012 in/in @Thickness 0.125 in
Melt Index of Compound	14 - 16 g/10 min @Load 2.16 kg, Temperature 230 °C	14 - 16 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	68.0 MPa	9860 psi	50 mm/min; ASTM D638
Elongation at Break	5.0 %	5.0 %	50 mm/min; ASTM D638
Tensile Modulus	2.10 GPa	305 ksi	50 mm/min; ASTM D638
Flexural Yield Strength	87.0 MPa	12600 psi	1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus	2.50 GPa	363 ksi	1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched	0.694 J/cm	1.30 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	144 °C @Thickness 3.20 mm	291 °F @Thickness 0.126 in	unannealed; ASTM D648