Ohio Carbon Blank OCB AR-06 EDM Grade Graphite
| Category | Carbon , Graphite |
| Manufacturer | Ohio Carbon Blank |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ohio Carbon Blank OCB AR-06 EDM Grade Graphite.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Available in a range of sizes and shapes.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Apparent Bulk Density | 1.76 g/cc | 0.0636 lb/in³ | |
| Particle Size | 12.0 µm | 12.0 µm | Average |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 55 | 55 | |
| Tensile Strength | 25.4 MPa | 3680 psi | |
| Flexural Strength | 44.8 MPa | 6500 psi | |
| Compressive Strength | 98.6 MPa | 14300 psi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 120 W/m-K | 833 BTU-in/hr-ft²-°F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.00127 ohm-cm | 0.00127 ohm-cm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Grain | Fine | |
| Suggested Application | Roughing Electrodes | |
| Suggested Applications | Forging Dies | |
| Large Cavity Molds | ||
| Large Die Casts | ||
| Large Extrusion Dies | ||
| Wear Resistance | Medium |
Users viewing this material also viewed the following:
- Chevron Phillips 1025 Extrusion Coating Resin (discontinued **)
- M. Holland Company LD800 LDPE (discontinued **)
- Kobe Steel KS100 Commercially Pure Titanium, Annealed
- SABIC Innovative Plastics LNP LUBRICOMP QCL34 PA6.10
- Teknor Apex Telcar® TL-1477B AUTO UV BLACK 111 Thermoplastic Elastomer
- A. Schulman FORMION™ FI 200 Non-Reinforced, Injection Molding Grade Ionomer / Nylon Alloy
- Dow Corning C6-570 LIQUID SILICONE RUBBER KIT
- DSM Stanyl® TE341 Nylon 46 (European Grade) (Cond)
Copyright © lookpolymers.com All Rights Reserved