- Objet FullCure® 930 Tango Plus Resin for Rapid Prototyping
Objet FullCure® 930 Tango Plus Resin for Rapid Prototyping
| Category | Polymer , Rapid Prototyping Polymer |
| Manufacturer | Objet |
| Trade Name | FullCure® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Objet FullCure® 930 Tango Plus Resin for Rapid Prototyping.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by American Precision Prototyping, LLC
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 27 | 27 | ASTM D2240 |
| Tensile Strength, Ultimate | 1.455 MPa | 211.0 psi | ASTM D412 |
| Tensile Strength, Yield | 0.146 MPa @Strain 20.0 % |
21.2 psi @Strain 20.0 % |
ASTM D413 |
| 0.185 MPa @Strain 30.0 % |
26.8 psi @Strain 30.0 % |
ASTM D413 | |
| 0.263 MPa @Strain 50.0 % |
38.1 psi @Strain 50.0 % |
ASTM D413 | |
| Elongation at Break | 218 % | 218 % | ASTM D412 |
| Tear Strength | 3.40 kN/m | 19.4 pli | ASTM D624 |
| Compression Set | 4.4 % @Temperature 75.0 °C, Time 79200 sec |
4.4 % @Temperature 167 °F, Time 22.0 hour |
ASTM D395 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Glass Transition Temp, Tg | -9.60 °C | 14.7 °F | DSC (-80°C+100°C) |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ross Flex | >150,000 |
Users viewing this material also viewed the following:
- Rogers Corporation R/bak® SS Cushion Mounting Materials, Supported Soft
- Lehmann & Voss LUVOCOM® 1105-8053/EM/BL PEEK, with glass fiber, easy flowing
- Ferro IX 2443 Passivation Glasses - High Voltage (Zn-B-Silicates)
- Indium Corp. Indalloy® 171 Pb-Sn Solder Alloy
- Teknor Apex Telcar® TL-2519G Thermoplastic Elastomer
- Daikin NEOFLON EC-6510 ETFE Coating Powder, White
- ExxonMobil Exceed™ 2227ED Metallocene Polyethylene Resin (European Grade)
Copyright © lookpolymers.com All Rights Reserved