Network Polymers Softflex® 8910
| Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Elastomer, Melt-Processible Rubber |
| Manufacturer | Network Polymers |
| Trade Name | Softflex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Network Polymers Softflex® 8910.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Softflex® Thermoplastic Elastomer AlloyInformation provided by Network Polymers Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.17 g/cc | 1.17 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.012 - 0.016 cm/cm @Thickness 3.17 mm |
0.012 - 0.016 in/in @Thickness 0.125 in |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.012 - 0.016 cm/cm @Thickness 3.17 mm |
0.012 - 0.016 in/in @Thickness 0.125 in |
ASTM D955 |
| Melt Flow | 25 g/10 min @Load 1.00 kg, Temperature 235 °C |
25 g/10 min @Load 2.20 lb, Temperature 455 °F |
Procedure A Condition Q; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 77 | 77 | Instantaneous; ASTM D2240 |
| Tensile Strength, Yield | 34.5 MPa | 5000 psi | chs 20 in/min; ASTM D412 |
| Elongation at Break | 535 % | 535 % | ASTM D412 |
| 50% Modulus | 0.00300 GPa | 0.435 ksi | ASTM D412 |
| 100% Modulus | 0.00470 GPa | 0.682 ksi | ASTM D412 |
| 300% Modulus | 0.00970 GPa | 1.41 ksi | ASTM D412 |
| Tear Strength | 87.5 kN/m | 499 pli | |
| Taber Abrasion, mg/1000 Cycles | 0.0551 | 0.0551 | H22 Wheel 1000 g load/1000 cycles; ASTM D3389 |
| Compression Set | 28 % @Temperature 100 °C |
28 % @Temperature 212 °F |
22 hours at 25% deflection; ASTM D395, Method B, |
Users viewing this material also viewed the following:
- DuPont™ Clysar® HP Polyolefin Shrink Packaging Film, 75 Gauge (discontinued **)
- Fainplast Compounds RE 412/L Rigid PVC, Extrusion
- SCG Chemicals EL-Proâ„¢ P701J Polypropylene Injection Molding
- Trelleborg Emerson & Cuming EP679 Patch Paste
- China Tungsten FeMo70Cu1 Ferro Molybdenum
- Clariant Renol 66G33HSL Nylon 66, 33% Glass Fiber Reinforced, Heat Stabilized, Lubricated
- Axiall 11890 Wire & Cable Flexible PVC
- Indium Corp. Indalloy 218 Silver Solder Alloy
Copyright © lookpolymers.com All Rights Reserved