Network Polymers Softflex® 7700
| Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Elastomer, Melt-Processible Rubber |
| Manufacturer | Network Polymers |
| Trade Name | Softflex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Network Polymers Softflex® 7700.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Softflex® Thermoplastic Elastomer AlloyInformation provided by Network Polymers Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.17 g/cc | 1.17 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.012 - 0.016 cm/cm @Thickness 3.17 mm |
0.012 - 0.016 in/in @Thickness 0.125 in |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.012 - 0.016 cm/cm @Thickness 3.17 mm |
0.012 - 0.016 in/in @Thickness 0.125 in |
ASTM D955 |
| Melt Flow | 25 g/10 min @Load 1.20 kg, Temperature 224 °C |
25 g/10 min @Load 2.65 lb, Temperature 435 °F |
Procedure A; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 72 - 82 | 72 - 82 | Instantaneous; ASTM D2240 |
| Tensile Strength, Yield | 34.5 MPa | 5000 psi | chs 20 in/min; ASTM D412 |
| Elongation at Break | 535 % | 535 % | ASTM D412 |
| 50% Modulus | 0.00300 GPa | 0.435 ksi | ASTM D412 |
| 100% Modulus | 0.00470 GPa | 0.682 ksi | ASTM D412 |
| 300% Modulus | 0.00970 GPa | 1.41 ksi | ASTM D412 |
| Tear Strength | 87.5 kN/m | 499 pli | |
| Compression Set | 28 % @Temperature 70.0 °C |
28 % @Temperature 158 °F |
22 hours at 25% deflection; ASTM D395, Method B, |
Users viewing this material also viewed the following:
- NYCOA 27/300SR Glass Filled Nylon 6
- SABIC Innovative Plastics LNP THERMOCOMP DX06094 PC (Europe-Africa-Middle East)
- SABIC Innovative Plastics NORYL PN275 PPE+PS
- Teknor Apex Telcar® TL-8431 Thermoplastic Elastomer
- A. Schulman POLYBATCH™ XAMF-500-T Process Aid Concentrate, Concentrate Based In LLDPE
- A. Schulman POLYFORT™ FPP 1606 Glass Filled Chemically Coupled Impact Copolymer Polypropylene
- Zircar Refractory Composites ASPA-2 Alumina-Silica Fiber Paper
- DuPont Teijin Films Teijin® Tetoron® U4 Polyester Film, 400 Gauge
- Overview of materials for PVC, Molded
- BASF Luranyl® KR 2456/3 Polyphenylene Ether + Styrene-Butadiene Blend
Copyright © lookpolymers.com All Rights Reserved