Network Polymers NPS 90-0802 Polystyrene
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified |
| Manufacturer | Network Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Network Polymers NPS 90-0802 Polystyrene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding Grade, High ImpactInformation provided by Network Polymers Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Melt Flow | 8.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
8.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
Procedure A Condition G; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell L | 47 | 47 | ASTM D785 |
| Tensile Strength at Break | 26.9 MPa | 3900 psi | chs 2 in/min; ASTM D638 |
| Elongation at Break | 45 % | 45 % | ASTM D638 |
| Tensile Modulus | 1.59 GPa | 230 ksi | chs 2 in/min; ASTM D638 |
| Flexural Modulus | 1.93 GPa | 280 ksi | Test Method I, Procedure B (chs speed 0.05 in/min); ASTM D790 |
| Izod Impact, Notched | 1.01 J/cm | 1.90 ft-lb/in | Test Method A (0.125 in bar); ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 81.1 °C | 178 °F | Annealed; ASTM D648 |
| Vicat Softening Point | 85.0 °C | 185 °F | ASTM D1525 |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPE A 8021 BLK , 37.5% Filler Content
- ExxonMobil LL 6235.19 Injection Molding Resin (discontinued **)
- Greene Tweed CHEMRAZ® 600 Perfluoroelastomer
- Silberline 4-Allâ„¢ E 3064AR
- Total PS CPDS 820 Flame Retardant Polystyrene
- Covestro Desmopan® 372 Thermoplastic Polyurethane
- AIM 95Sn/3.5Ag/1.5In Solder for Photonic Packaging
- Ashley Polymers Ashlene® 1420B Polycarbonate, 20% Glass Reinforced
- DuPont Teijin Films Melinex® 516R Polyester Film
Copyright © lookpolymers.com All Rights Reserved