NatureWorks® Ingeo™ 4043D General Purpose Film Grade Biopolymer
| Category | Polymer , Film , Renewable/Recycled Polymer , Thermoplastic , Polylactic Acid (PLA) Biopolymer |
| Manufacturer | NatureWorks LLC |
| Trade Name | Ingeo™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NatureWorks® Ingeo™ 4043D General Purpose Film Grade Biopolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ingeo 4043D can be converted into a biaxially oriented film with use temperatures up to 265ºF (130ºC). This film has excellent optics, good machinability and excellent twist and deadfold. These properties make 4043D film an ideal candidate for candy twist wrap and other packaging applications. Additional properties include advantageous barrier to flavor and grease and superior oil resistance.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ASTM D1505 |
| Moisture Vapor Transmission | 13.8 - 15.7 cc-mm/m²-24hr-atm | 35.1 - 39.9 cc-mil/100 in²-24hr-atm | ASTM F1249 |
| Oxygen Transmission | 25.6 - 27.6 cc-mm/m²-24hr-atm | 65.0 - 70.1 cc-mil/100 in²-24hr-atm | ASTM D3985 |
| Carbon Dioxide Transmission | 106 - 118 cc-mm/m²-24hr-atm | 269 - 300 cc-mil/100 in²-24hr-atm | NatureWorks test |
| Viscosity Measurement | 4.0 @Temperature 30.0 °C |
4.0 @Temperature 86.0 °F |
Relative viscosity; 1.0 g/dl chloroform |
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 210 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 410 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 160 % | 160 % | ASTM D882 |
| Film Elongation at Break, TD | 100 % | 100 % | ASTM D882 |
| Secant Modulus, MD | 3.30 GPa | 479 ksi | ASTM D882 |
| Secant Modulus, TD | 3.900 GPa | 565.7 ksi | ASTM D882 |
| Elmendorf Tear Strength, MD | 0.591 g/micron | 15.0 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 0.512 g/micron | 13.0 g/mil | ASTM D1922 |
| Film Tensile Strength at Break, MD | 110 MPa | 16000 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 145 MPa | 21000 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 145 - 160 °C | 293 - 320 °F | ASTM D3418 |
| Maximum Service Temperature, Air | 130 °C | 266 °F |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 2.1 % | 2.1 % | ASTM D1003 |
| Gloss | 90 % | 90 % | 20°; ASTM D1003 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 180 °C | 356 °F | |
| Adapter Temperature | 200 °C | 392 °F | |
| Die Temperature | 200 °C | 392 °F | |
| Melt Temperature | 202 - 218 °C | 396 - 424 °F | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm |
Users viewing this material also viewed the following:
- Plansee WL20 Lanthanum Oxide-doped Tungsten
- Network Polymers NPS 90-0304 F Super High Impact Polystyrene
- Solvay Specialty Polymers Torlon® 4200 Polyamide-imide (PAI) (Unverified Data**)
- SABIC Innovative Plastics LNP LUBRICOMP RL004S PA 66 (Europe-Africa-Middle East)
- Sekisui PIOCELAN TOPF-30DUB Black (Low VOC, Low odor) Flame Retardant Moldable Polymer Foam
- Special Metals INCONEL® 706 Precipitation Hardening Alloy, Hot Finished Rod, 3 Part Heat Treatment, 0.562 inch (14.3 mm) Diameter
- Silberline Silvex® 440-15-C
- A. Schulman POLYPUR™ FPU 1152C Thermoplastic Polyurethane
- Chosun Refractories RSP-M Blast Furnace Runner Refractory
- Pasargad Polymer Peyvand Pasamid 3P-M1130B Nylon 6, 30% Glass Fiber Reinforced
Copyright © lookpolymers.com All Rights Reserved