NOVA Chemicals Surpass® RMs539-U Octene sMDPE Rotational Molding Film

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , MDPE , Linear Medium Density Polyethylene (LMDPE), Rotational Molded
Manufacturer	NOVA Chemicals
Trade Name	Surpass®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	NOVA Chemicals Surpass® RMs539-U Octene sMDPE Rotational Molding Film.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Features: Octene copolymerExceptional low temperature impact propertiesOutstanding stiffnessBroad processing windowSuperior whiteness for improved part appearanceEasy mold releaseNSF listed for Standards 14, 24 and 61 Low viscosity for exceptional processability, shorter cycle times, and energy savings Applications: OEM custom and proprietary components Recreational and leisure equipment Marine productsContainers, septic tanks, and fish boxesInformation provided by Nova Chemicals

Physical Properties	Metric	English	Comments
Density	0.939 g/cc	0.0339 lb/in³	Compression Molded; ASTM D792
ESCR 10% Igepal®	>= 50 hour	>= 50 hour	Compression Molded; ARM Method
Melt Flow	5.2 g/10 min @Load 2.16 kg, Temperature 190 °C	5.2 g/10 min @Load 4.76 lb, Temperature 374 °F	Compression Molded; ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	61	61	Compression Molded; ASTM D2240
Tensile Strength, Ultimate	27.1 MPa	3930 psi	Compression Molded; ASTM D638
Tensile Strength, Yield	20.0 MPa	2900 psi	Compression Molded; ASTM D638
Elongation at Break	920 %	920 %	Compression Molded; ASTM D638
Elongation at Yield	11 %	11 %	Compression Molded; ASTM D638
Flexural Modulus	0.740 GPa	107 ksi	Compression Molded; ASTM D790
Impact Test	27.0 J @Thickness 3.17 mm, Temperature -40.0 °C	19.9 ft-lb @Thickness 0.125 in, Temperature -40.0 °F	Rotational Molded, Instrumented
	54.0 J @Thickness 3.17 mm, Temperature -40.0 °C	39.8 ft-lb @Thickness 0.125 in, Temperature -40.0 °F	Rotational Molded; ARM Method
	108 J @Thickness 3.17 mm, Temperature -40.0 °C	79.7 ft-lb @Thickness 0.125 in, Temperature -40.0 °F	Rotational Molded, Instrumented
	230 J @Thickness 3.17 mm, Temperature -40.0 °C	170 ft-lb @Thickness 0.125 in, Temperature -40.0 °F	Rotational Molded; ARM Method

Thermal Properties	Metric	English	Comments
Melting Point	125 °C	257 °F	Compression Molded; ASTM E794
Deflection Temperature at 0.46 MPa (66 psi)	60.0 °C	140 °F	Compression Molded; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	42.0 °C	108 °F	Compression Molded; ASTM D648
Vicat Softening Point	121 °C	250 °F	Compression Molded; ASTM D1525