- NOVA Chemicals Surpass® FPs117-D Octene sLLDPE Film Resin (discontinued **)
NOVA Chemicals Surpass® FPs117-D Octene sLLDPE Film Resin (discontinued **)
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NOVA Chemicals Surpass® FPs117-D Octene sLLDPE Film Resin
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Lamination Film, coextruded sealant layer, high toughness filmInformation provided by Nova Chemicals
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in³ | ASTM D792 |
| Thickness | 25.0 microns | 0.984 mil | |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 9.03 MPa | 1310 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 9.03 MPa | 1310 psi | ASTM D882 |
| Film Elongation at Yield, MD | 550 % | 550 % | ASTM D638 |
| Film Elongation at Yield, TD | 725 % | 725 % | ASTM D882 |
| Puncture Energy | 1.75 J | 1.29 ft-lb | Low Friction Puncture |
| Elmendorf Tear Strength MD | 320 g | 320 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 480 g | 480 g | ASTM D1922 |
| Dart Drop Test | 800 g | 1.76 lb | ASTM D1709/A |
| Film Tensile Strength at Break, MD | 43.0 MPa | 6240 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 34.0 MPa | 4930 psi | ASTM D882 |
| 1% Secant Modulus, MD | 134.96 MPa | 19575 psi | ASTM D882 |
| 1% Secant Modulus, TD | 144.96 MPa | 21025 psi | ASTM D882 |
| Heat Seal Strength Initiation Temperature | 100 °C | 212 °F | 2N |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 17 % | 17 % | ASTM D1003 |
| Gloss | 32 % | 32 % | at 45°; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 185 - 200 °C | 365 - 392 °F |
Users viewing this material also viewed the following:
- Greene Tweed Fluoroelastomer 931 FKM
- SABIC Innovative Plastics LNP VERTON MVL36SX0 PP (Europe-Africa-Middle East)
- A. Schulman POLYFORT™ FPP 1285U Glass Filled, UV Stable Impact Copolymer Polypropylene
- Cheng Yu Plastic N6CV1 Flame Retardant Nylon 6, 10% Mineral Reinforced
- Chosun Refractories APC-120 Acid-proof Castable
- DuPont Teijin Films Melinex® 565 Polyester Film
- BASF Heligoen® Blue K 7090 Color Additive
- Arkema Group Evatane® 1005 VN 2 Ethylene Vinyl Acetate
- Ashley Polymers Ashlene® 830L-30G Nylon 6, 30% Glass Reinforced
- Bulk Molding Compounds BMC T40(20) Die Casting Replacement Grade Molding Compound
Copyright © lookpolymers.com All Rights Reserved