NOVA Chemicals Sclair® FP112-A Octene VLDPE Film Resin

Category	Polymer , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer	NOVA Chemicals
Trade Name	Sclair®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	NOVA Chemicals Sclair® FP112-A Octene VLDPE Film Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Features: Low seal initiation temperatureHigh toughnessVery good optical propertiesComplies with U.S. FDA 21 CFR 177.1520 (c) 3.2a Low gel Applications: Sealant and lamination film for food packagingInformation provided by Nova Chemicals

Physical Properties	Metric	English	Comments
Density	0.912 g/cc	0.0329 lb/in³	ASTM D792
Thickness	51.0 microns	2.01 mil
Melt Flow	0.90 g/10 min @Load 2.16 kg, Temperature 190 °C	0.90 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	7.38 MPa	1070 psi	ASTM D882
Film Tensile Strength at Yield, TD	7.38 MPa	1070 psi	ASTM D882
Film Elongation at Yield, MD	640 %	640 %	ASTM D638
Film Elongation at Yield, TD	890 %	890 %	ASTM D882
Puncture Energy	3.162 J	2.332 ft-lb	Low Friction Puncture
Elmendorf Tear Strength MD	710 g	710 g	ASTM D1922
Elmendorf Tear Strength TD	1010 g	1010 g	ASTM D1922
Dart Drop Test	>= 1000 g	>= 2.20 lb	ASTM D1709/A
Film Tensile Strength at Break, MD	49.0 MPa	7110 psi	ASTM D882
Film Tensile Strength at Break, TD	54.0 MPa	7830 psi	ASTM D882
1% Secant Modulus, MD	114.0 MPa	16530 psi	ASTM D882
1% Secant Modulus, TD	123.0 MPa	17840 psi	ASTM D882
Heat Seal Strength Initiation Temperature	72.0 °C	162 °F

Optical Properties	Metric	English	Comments
Haze	8.7 %	8.7 %	ASTM D1003
Gloss	63 %	63 %	at 45°; ASTM D2457