NOVA Chemicals Sclair® 58D HDPE Blow Molding Resin (discontinued **)

Category	Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Blow Molding Grade
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	NOVA Chemicals Sclair® 58D HDPE Blow Molding Resin (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Features: Good ESCR, high stiffness, good impact strength, slightly tougher alternative to Sclair 58A.Applications: Small part blow molding, food, pharmaceuticals, HIC containers.Data provided by the manufacturer.

Physical Properties	Metric	English	Comments
Density	0.957 g/cc	0.0346 lb/in³	ASTM D792
Environmental Stress Crack Resistance	150 hour	150 hour	F50, Condition A, ASTM D1693, 100% Igepal
Melt Flow	0.29 g/10 min @Load 2.16 kg, Temperature 190 °C	0.29 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	67	67	ASTM D2240
Tensile Strength, Yield	29.0 MPa	4210 psi	ASTM D638
Elongation at Break	960 %	960 %	at 50 mm/min; ASTM D638
Flexural Modulus	1.17 GPa	170 ksi	ASTM D790

Thermal Properties	Metric	English	Comments
Vicat Softening Point	125 °C	257 °F	ASTM D1525
Brittleness Temperature	<= -70.0 °C	<= -94.0 °F	ASTM D696

Processing Properties	Metric	English	Comments
Melt Temperature	160 - 205 °C	320 - 401 °F