NOVA Chemicals Novapol® TF-Y826-CP Hexene LLDPE Film Resin

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Hexene, Film Grade
Manufacturer	NOVA Chemicals
Trade Name	Novapol®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	NOVA Chemicals Novapol® TF-Y826-CP Hexene LLDPE Film Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Film Properties. Features: Good stiffness, intended for narrow die gaps, high strength and toughness.Applications: Industrial bags, industrial packaging.Data provided by the manufacturer.

Physical Properties	Metric	English	Comments
Density	0.926 g/cc	0.0335 lb/in³	ASTM D792
Thickness	38.1 microns	1.50 mil
Melt Flow	0.80 g/10 min @Load 2.16 kg, Temperature 190 °C	0.80 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	13.0 MPa	1890 psi	ASTM D882
Film Tensile Strength at Yield, TD	14.0 MPa	2030 psi	ASTM D882
Film Elongation at Break, MD	600 %	600 %	ASTM D882
Film Elongation at Break, TD	700 %	700 %	ASTM D882
Secant Modulus, MD	0.210 GPa	30.5 ksi	ASTM D882
Secant Modulus, TD	0.250 GPa	36.3 ksi	ASTM D882
Coefficient of Friction	>= 0.40	>= 0.40	ASTM D1894
Elmendorf Tear Strength, MD	6.30 g/micron	160 g/mil	ASTM D1922
Elmendorf Tear Strength, TD	21.7 g/micron	551 g/mil	ASTM D1922
Dart Drop	5.50 g/micron	140 g/mil	F 50; ASTM D1709/A
Film Tensile Strength at Break, MD	44.0 MPa	6380 psi	ASTM D882
Film Tensile Strength at Break, TD	32.0 MPa	4640 psi	ASTM D882

Optical Properties	Metric	English	Comments
Haze	18 % @Thickness 0.0250 mm	18 % @Thickness 0.000984 in	ASTM D1003
Gloss	39 %	39 %	45°; 1 mil; ASTM D1894

Processing Properties	Metric	English	Comments
Melt Temperature	195 - 220 °C	383 - 428 °F