NOVA Chemicals Novapol® LF-0225-B LDPE Clarity Film Resin (discontinued **)

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	NOVA Chemicals Novapol® LF-0225-B LDPE Clarity Film Resin (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Features: High optical clarityExcellent processability Applications: Produce and bakery filmLinersTextile packaging filmGeneral packaging requiring high clarity filmInformation provided by Nova Chemicals

Physical Properties	Metric	English	Comments
Density	0.924 g/cc	0.0334 lb/in³	ASTM D792
Thickness	38.0 microns	1.50 mil
Melt Flow	2.2 g/10 min @Load 2.16 kg, Temperature 190 °C	2.2 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	11.0 MPa	1600 psi	ASTM D882
Film Tensile Strength at Yield, TD	9.65 MPa	1400 psi	ASTM D882
Film Elongation at Yield, MD	330 %	330 %	ASTM D882
Film Elongation at Yield, TD	520 %	520 %	ASTM D882
Coefficient of Friction	<= 0.15	<= 0.15	ASTM D1894
Elmendorf Tear Strength MD	228 g	228 g	ASTM D1922
Elmendorf Tear Strength TD	264 g	264 g	ASTM D1922
Dart Drop Test	120 g	0.265 lb	F<sub>50</sub>; ASTM D1709/A
Film Tensile Strength at Break, MD	20.99 MPa	3045 psi	ASTM D882
Film Tensile Strength at Break, TD	15.00 MPa	2175 psi	ASTM D882
1% Secant Modulus, MD	215 MPa	31200 psi	ASTM D882
1% Secant Modulus, TD	220 MPa	31900 psi	ASTM D882

Optical Properties	Metric	English	Comments
Haze	6.5 %	6.5 %	ASTM D1003
Gloss	70 %	70 %	at 45°; ASTM D2457
Transmission, Visible	90 %	90 %	clear; thickness not quantified