Multibase SILASTIC® C7-4565 DICUP R Dow-Corning Biomedical Grade ETR Elastomer

Category Polymer , Thermoset , Silicone
Manufacturer Multibase
Trade Name SILASTIC®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Multibase SILASTIC® C7-4565 DICUP R Dow-Corning Biomedical Grade ETR Elastomer.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Information provided by Multibase
Mechanical Properties Metric English Comments
Hardness, Shore A 61
61
as molded
67
67
post cured- 2 hours at 177°C
75
75
post cured- 4 hours at 204°C
Tensile Strength, Ultimate 7.31 MPa
1060 psi
post cured- 4 hours at 204°C
8.20 MPa
1190 psi
as molded
8.34 MPa
1210 psi
post cured- 2 hours at 177°C
Tensile Strength, Yield 3.28 MPa
475 psi
at 200%, as molded
3.28 MPa
475 psi
at 200%, post cured- 2 hours at 177°C
3.73 MPa
541 psi
200%, post cured- 4 hours at 204°C
Elongation at Break 513 %
513 %
post cured- 4 hours at 204°C
608 %
608 %
post cured- 2 hours at 177°C
665 %
665 %
as molded
Tear Strength 36.5 kN/m
208 pli
post cured- 4 hours at 204°C; Die B
40.0 kN/m
228 pli
post cured- 2 hours at 177°C; Die B
43.1 kN/m
246 pli
as molded; Die B