Multibase Multi-Flex® A 4001 LC Black TPE Thermoplastic Elastomer
| Category | Polymer , Thermoplastic , Elastomer, TPE |
| Manufacturer | Multibase |
| Trade Name | Multi-Flex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Multibase Multi-Flex® A 4001 LC Black TPE Thermoplastic Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Heat Resistance, HighOzone ResistantCompression Set, Low Forms: PelletsProcessing Method:Injection Molding Information provided by Multibase
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.07 g/cc | 1.07 g/cc | ASTM 792 |
| Linear Mold Shrinkage | 0.015 cm/cm | 0.015 in/in | ASTM D955 |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 33 | 33 | 10 seconds; ASTM D2240 |
| Tensile Strength, Yield | 5.50 MPa | 798 psi | Elastic; ASTM D412 |
| 0.827 MPa @Strain 100 % |
120 psi @Strain 100 % |
ASTM D412 | |
| Elongation at Break | 600 % | 600 % | Elastic; ASTM D412 |
| Tear Strength | 17.5 kN/m | 100 pli | ASTM D624 |
| Compression Set | 11 % | 11 % | 73°F, 70 hours; ASTM D395 |
| 39 % | 39 % | 158°F, 70 hours; ASTM D395 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Flame Spread | 38 mm/min | 1.5 in/min | VSS-302 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 210 °C | 410 °F | |
| Front Barrel Temperature | 227 °C | 440 °F | |
| Nozzle Temperature | 235 °C | 455 °F | |
| Mold Temperature | 51.7 °C | 125 °F | |
| Moisture Content | <= 0.060 % | <= 0.060 % |
Users viewing this material also viewed the following:
- Lucobit Lucobit® 1233 Ethylene Copolymer Bitumen
- SABIC Innovative Plastics LNP STAT-KON EX99689C PEI
- Techmer ES HiFill® PA6 GF50 RM LE 50% Glass Filled (Dry)
- Techmer ES HiFill® PA6/6 GF/M40 B1 BK 40% Glass/Mineral Fiber Filled
- Saint-Gobain Norton® T-100 Virgin Skived PTFE Film (0.005" thick)
- Skamol Group VERMICAST 14-100 Insulating Castable
- Lubrizol ESTANE® X1014 Ether Based Thermoplastic Polyurethane (European Grade)
- Adamas Adalon® 998 PTFE, Turquoise
- BASF Procom® D 1146 Polypropylene
- Haynes Hastelloy® C-4 alloy, welded plate 12.7 mm (1/2 in.) thick, aged 10 hours at 649°C (1200°F)
Copyright © lookpolymers.com All Rights Reserved