Mitsui AURUM® JGN3030 Thermoplastic Polyimide Resin, Amorphous  (discontinued **)

Category Polymer , Thermoplastic , Polyimide, Thermoplastic
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Mitsui AURUM® JGN3030 Thermoplastic Polyimide Resin, Amorphous  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
AURUM® is an easy melt, processable and recyclable thermoplastic polyimide resin that provides continuous service temperatures to 465° F in its amorphous state and up to 550° F when annealed to its semicrystalline state. In addition, it displays low outgassing, superior radiation resistance and excellent chemical resistance properties.Applications: Components for automotive and aircraft enginesTransmissionFarming, off-road and construction equipmentIndustrial machineryElectric motors, pumps and compressorsBusiness machines such as laser pointers and high speed copy machinesElectronic and semiconductor transport mediaAnalytical and medical equipmentConveyors and textile equipmentInformation provided by Mitsui.
Physical Properties Metric English Comments
Density 1.56 g/cc
0.0564 lb/in³
ASTM D792
Water Absorption 0.23 %
0.23 %
24 hours; ASTM D570
Moisture Absorption at Equilibrium 0.10 %
0.10 %
24 hours, 23°C, 60% RH
Linear Mold Shrinkage 0.0044 cm/cm
0.0044 in/in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell M 104
104
ASTM D785
Hardness, Rockwell R 128
128
ASTM D785
Tensile Strength at Break 164.8 MPa
23900 psi
ASTM D638
Tensile Strength, Ultimate 105.9 MPa

@Temperature 150 °C
15360 psi

@Temperature 302 °F
ASTM D638
Elongation at Break 3.0 %
3.0 %
ASTM D638
4.0 %

@Temperature 150 °C
4.0 %

@Temperature 302 °F
ASTM D638
Flexural Strength 241 MPa
35000 psi
ASTM D790
173 MPa

@Temperature 150 °C
25100 psi

@Temperature 302 °F
ASTM D790
Flexural Modulus 9.51 GPa
1380 ksi
ASTM D790
8.04 GPa

@Temperature 150 °C
1170 ksi

@Temperature 302 °F
ASTM D790
Compressive Strength 88.3 MPa

@Temperature 150 °C
12800 psi

@Temperature 302 °F
JIS K7208
188 MPa

@Temperature 23.0 °C
27300 psi

@Temperature 73.4 °F
JIS K7208
Compressive Modulus 2.26 GPa
328 ksi
At 150°C; JIS K7208
3.14 GPa
455 ksi
At 23°C; JIS K7208
Shear Strength 76.5 MPa

@Temperature 150 °C
11100 psi

@Temperature 302 °F
JIS K7214
81.4 MPa

@Temperature 23.0 °C
11800 psi

@Temperature 73.4 °F
JIS K7214
Izod Impact, Notched 1.18 J/cm
2.20 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
CTE, linear 17.0 µm/m-°C

@Temperature 23.0 °C
9.44 µin/in-°F

@Temperature 73.4 °F
MD; ASTM D696
17.0 µm/m-°C

@Temperature 200 °C
9.44 µin/in-°F

@Temperature 392 °F
MD; ASTM D696
CTE, linear, Transverse to Flow 53.0 µm/m-°C

@Temperature 23.0 °C
29.4 µin/in-°F

@Temperature 73.4 °F
ASTM D696
53.0 µm/m-°C

@Temperature 200 °C
29.4 µin/in-°F

@Temperature 392 °F
ASTM D696
Specific Heat Capacity 0.960 J/g-°C

@Temperature 23.0 °C
0.229 BTU/lb-°F

@Temperature 73.4 °F
By DSC
0.960 J/g-°C

@Temperature 100 °C
0.229 BTU/lb-°F

@Temperature 212 °F
By DSC
1.34 J/g-°C

@Temperature 300 °C
0.320 BTU/lb-°F

@Temperature 572 °F
By DSC
Thermal Conductivity 0.349 W/m-K
2.41 BTU-in/hr-ft²-°F
Melting Point 388 °C
730 °F
Maximum Service Temperature, Air 245 °C
473 °F
Heat distortion temperature, load unknown; ASTM D648
Glass Transition Temp, Tg 250 °C
482 °F
By DSC
Flammability, UL94 V-0

@Thickness 0.400 mm
V-0

@Thickness 0.0157 in
all color
Electrical Properties Metric English Comments
Surface Resistance 1.00e+16 ohm
1.00e+16 ohm
Dielectric Constant 3.7

@Frequency 1e+6 Hz
3.7

@Frequency 1e+6 Hz
ASTM D150
3.8

@Frequency 1000 Hz
3.8

@Frequency 1000 Hz
ASTM D150
Dissipation Factor 0.0012

@Frequency 1000 Hz
0.0012

@Frequency 1000 Hz
ASTM D150
0.0036

@Frequency 1e+6 Hz
0.0036

@Frequency 1e+6 Hz
ASTM D150
Processing Properties Metric English Comments
Processing Temperature 390 - 420 °C
734 - 788 °F
Injection molding, extrusion