Master Bond EP30LTE-LO Dimensionally Stable Low Outgassing Two Part Epoxy
| Category | Polymer , Thermoset , Epoxy , Epoxy, Cast, Unreinforced |
| Manufacturer | Master Bond Inc. |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Master Bond EP30LTE-LO Dimensionally Stable Low Outgassing Two Part Epoxy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Master Bond Polymer System EP30LTE-LO is a thermal shock resistant epoxy resin system with low thermal expansion properties and dimensional stability for high performance bonding, sealing and casting. This two component epoxy resin compound, cures readily at ambient or more quickly at elevated temperatures, significant reduction in the high thermal expansion coefficients characteristic of epoxies and all other organic polymers while retaining their advantageous properties and ease of processability.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Absorption | <= 1.0 % @Time 86400 sec |
<= 1.0 % @Time 24.0 hour |
|
| Viscosity | 10 - 110 cP | 10 - 110 cP | Part B |
| 45000 - 75000 cP | 45000 - 75000 cP | Part A |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | >= 34.5 MPa | >= 5000 psi | |
| Elongation at Break | <= 3.0 % | <= 3.0 % | |
| Adhesive Bond Strength | >= 6.89 MPa | >= 1000 psi | Shear Al/Al |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 12.0 µm/m-°C | 6.67 µin/in-°F | |
| Thermal Conductivity | >= 0.720 W/m-K | >= 5.00 BTU-in/hr-ft²-°F | |
| Maximum Service Temperature, Air | 121 °C | 250 °F | |
| Minimum Service Temperature, Air | -51.1 °C | -60.0 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | |
| Dielectric Constant | 4.1 @Frequency 106 Hz |
4.1 @Frequency 106 Hz |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 2880 min | 48.0 hour | 85% maximum strength developed within |
| 120 - 240 min @Temperature 100 °C |
2.00 - 4.00 hour @Temperature 212 °F |
||
| Pot Life | 40 - 60 min | 40 - 60 min | 200 gram mass |
| Shelf Life | 6.00 Month | 6.00 Month | in unopened containers |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Mixing Ratio (A to B) | 10/1 |
Users viewing this material also viewed the following:
- LATI LARPEEK 50 G/40 40% Glass Reinforced Polyetheretherketone (PEEK) (discontinued **)
- SABIC Innovative Plastics Valox® 815 PBT
- SABIC Innovative Plastics XYLEX X7300CL PC+POLYESTER (Asia Pacific)
- Teknor Apex Tekbond® TB 1176A Thermoplastic Elastomer
- Teknor Apex Telcar® TL-1025-75 Thermoplastic Elastomer
- Formosa Plastics Formolene® 6335N Impact Copolymer Polypropylene
- Arkema Group Rilsan® MB 3945 Nylon 11, Rotomolding Grade (Conditioned)
- 3M Dyneon™ PVDF 31008/0009 Polyvinylidene Fluoride (discontinued **)
Copyright © lookpolymers.com All Rights Reserved