Category | Polymer , Film , Thermoplastic , Polypropylene (PP) , Polypropylene, Sheet/Thermoforming Grade |
Manufacturer | Mapal Plastics |
Trade Name | Maplon |
Port | Shanghai port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | Mapal Plastics Maplon Type D Polypropylene Sheet.pdf ![]() |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Specific Gravity | 0.910 g/cc | 0.910 g/cc | |
Thickness | 500 microns | 19.7 mil | |
Surface Tension | >= 48 dynes/cm | >= 48 dynes/cm | After 2 months from production |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Film Tensile Strength at Yield, MD | 30.0 MPa @Temperature 23.0 °C |
4350 psi @Temperature 73.4 °F |
ASTM D638 |
Film Tensile Strength at Yield, TD | 29.0 MPa @Temperature 23.0 °C |
4210 psi @Temperature 73.4 °F |
ASTM D638 |
Film Elongation at Break, MD | >= 600 % @Temperature 23.0 °C |
>= 600 % @Temperature 73.4 °F |
ASTM D638 |
Film Elongation at Break, TD | >= 600 % @Temperature 23.0 °C |
>= 600 % @Temperature 73.4 °F |
ASTM D638 |
Film Elongation at Yield, MD | 24 % @Temperature 23.0 °C |
24 % @Temperature 73.4 °F |
ASTM D638 |
Film Elongation at Yield, TD | 23 % @Temperature 23.0 °C |
23 % @Temperature 73.4 °F |
ASTM D638 |
Modulus of Elasticity | 0.280 GPa @Temperature 23.0 °C |
40.6 ksi @Temperature 73.4 °F |
MD/TD; ASTM D638 |
Tear Strength | <= 130 kN/m | <= 742 pli | Mapal internal method |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
Vicat Softening Point | 136 °C | 277 °F | ASTM D1525 |
Heat Distortion Temperature | 79.0 °C | 174 °F | ASTM D648 |