- Manifattura Cattaneo VESPEL® SP21 Polyimide
Manifattura Cattaneo VESPEL® SP21 Polyimide
| Category | Polymer , Thermoplastic , Polyimide, Thermoplastic |
| Manufacturer | Manifattura Cattaneo spa |
| Trade Name | VESPEL® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Manifattura Cattaneo VESPEL® SP21 Polyimide.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Manifattura Cattaneo products are available in semi-finished forms such as bars, profiles, sheets and plates.Information provided by Manifattura Cattaneo s.p.a.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.51 g/cc | 0.0546 lb/in³ | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.80 - 1.1 % @Temperature 23.0 °C |
0.80 - 1.1 % @Temperature 73.4 °F |
50% RH; ASTM D570 |
| Water Absorption at Saturation | 0.57 % | 0.57 % | ASTM D570 |
| Deformation | 0.70 % @Time 86400 sec, Pressure 100 MPa |
0.70 % @Time 24.0 hour, Pressure 14500 psi |
ASTM D621 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 66.0 MPa | 9570 psi | ASTM D638 |
| Elongation at Break | 4.5 % | 4.5 % | ASTM D638 |
| Tensile Modulus | 2.62 GPa | 380 ksi | ASTM D638 |
| Flexural Strength | 110 MPa | 16000 psi | ASTM D790 |
| Compressive Yield Strength | 29.0 MPa @Strain 1.00 %, Time 3.60e+6 sec |
4210 psi @Strain 1.00 %, Time 1000 hour |
ASTM D695 |
| Compressive Modulus | 2.895 GPa | 419.9 ksi | ASTM D695 |
| Poissons Ratio | 0.41 | 0.41 | |
| Izod Impact, Notched (ISO) | 0.0430 kJ/m² | 0.0205 ft-lb/in² | ASTM D256 |
| Izod Impact, Unnotched (ISO) | 0.320 kJ/m² | 0.152 ft-lb/in² | ASTM D256 |
| Coefficient of Friction, Dynamic | 0.24 | 0.24 | on polished steel; MPC Test |
| Coefficient of Friction, Static | 0.30 | 0.30 | on polished steel; MPC Test |
| K Factor (Wear Factor) | 0.43 | 0.43 | µm/s. PV = 0.1 MPa-m/s; max P = 30 MPa; MPC Test |
| Limiting Pressure Velocity | 12.0 MPa-m/sec | 343000 psi-ft/min | without lubrication; MPC Test |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 49.0 µm/m-°C @Temperature 23.0 - 100 °C |
27.2 µin/in-°F @Temperature 73.4 - 212 °F |
|
| Thermal Conductivity | 0.870 W/m-K | 6.04 BTU-in/hr-ft²-°F | ASTM D177 |
| Maximum Service Temperature, Air | 395 °C | 743 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 360 °C | 680 °F | ASTM D648-45 |
| Flammability, UL94 | V-0 | V-0 | |
| Oxygen Index | 49 % | 49 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | ASTM D257 |
| Dielectric Constant | 13.41 @Frequency 1.00e+6 Hz |
13.41 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 9.48 kV/mm @Thickness 2.00 mm |
241 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Dielectric Loss Index | 0.0106 @Frequency 1.00e+6 Hz |
0.0106 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Compliance Properties | Metric | English | Comments |
|---|---|---|---|
| FDA | No | No |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Dark Gray | |
| UV Resistance | N |
Users viewing this material also viewed the following:
- Multibase Nylex™ 2185 HFX Natural Polyamide + PP
- LyondellBasell Montell 12C01G2 Clarity LLDPE
- Karina 752D02/101-AT-IS Yellow PVC Compound
- Diamond Polymers ABS 7500E
- Diamond Polymers NPP25-1201 TF10 10% Talc Filled Copolymer Polypropylene
- Eurostar Starflam MF0044 PP, Glass Fiber Filled, Flame Retardant, Injection Molded
- Dow INSPIRE™ 404 Performance Polymer
- 3M Cushion-Mount™ E1840 Plus Plate Mounting Tapes with Easy Mount Adhesive and High Plateside Adhesion
- LG Chemical LUPOY SR-3108F High Flow Modified PC, 10% Mineral Fillers, High Reflectivity, Flame Retardant
Copyright © lookpolymers.com All Rights Reserved