Manifattura Cattaneo RULON® J Polytetrafluoroethylene
| Category | Polymer , Thermoplastic , Fluoropolymer , PTFE |
| Manufacturer | Manifattura Cattaneo spa |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Manifattura Cattaneo RULON® J Polytetrafluoroethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Manifattura Cattaneo products are available in semi-finished forms such as bars, profiles, sheets and plates.Information provided by Manifattura Cattaneo s.p.a.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.95 g/cc | 0.0704 lb/in³ | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.00 % @Temperature 23.0 °C |
0.00 % @Temperature 73.4 °F |
50% RH; ASTM D570 |
| Water Absorption at Saturation | 0.30 % | 0.30 % | ASTM D570 |
| Deformation | 3.0 % @Time 86400 sec, Pressure 100 MPa |
3.0 % @Time 24.0 hour, Pressure 14500 psi |
ASTM D621 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 60 | 60 | ASTM D 2240 |
| Tensile Strength at Break | 13.8 MPa | 2000 psi | ASTM D638 |
| Elongation at Break | 180 % | 180 % | ASTM D638 |
| Compressive Yield Strength | 3.60 MPa @Strain 1.00 %, Time 3.60e+6 sec |
522 psi @Strain 1.00 %, Time 1000 hour |
ASTM D695 |
| Compressive Modulus | 0.420 GPa | 60.9 ksi | ASTM D695 |
| Coefficient of Friction, Dynamic | 0.20 | 0.20 | on polished steel; MPC Test |
| Coefficient of Friction, Static | 0.12 | 0.12 | on polished steel; MPC Test |
| K Factor (Wear Factor) | 0.65 | 0.65 | µm/s. PV = 0.1 MPa-m/s; max P = 5.2 MPa; MPC Test |
| Limiting Pressure Velocity | 0.260 MPa-m/sec | 7420 psi-ft/min | without lubrication; MPC Test |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 122 µm/m-°C @Temperature 23.0 - 100 °C |
67.8 µin/in-°F @Temperature 73.4 - 212 °F |
|
| CTE, linear, Transverse to Flow | 93.0 µm/m-°C @Temperature 23.0 °C |
51.7 µin/in-°F @Temperature 73.4 °F |
|
| Thermal Conductivity | 0.240 W/m-K | 1.67 BTU-in/hr-ft²-°F | ASTM D177 |
| Maximum Service Temperature, Air | 288 °C | 550 °F | |
| Minimum Service Temperature, Air | -240 °C | -400 °F | |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 8.20e+20 ohm-cm | 8.20e+20 ohm-cm | ASTM D257 |
| Surface Resistance | 6.30e+18 ohm | 6.30e+18 ohm | ASTM D257 |
| Dielectric Constant | 2.4 @Frequency 1.00e+6 Hz |
2.4 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 17.9 kV/mm @Thickness 2.00 mm |
455 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Dielectric Loss Index | 0.0015 @Frequency 1.00e+6 Hz |
0.0015 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Compliance Properties | Metric | English | Comments |
|---|---|---|---|
| FDA | No | No |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Dull Gold | |
| UV Resistance | Y |
Users viewing this material also viewed the following:
- Mytex Polymers AN16L(W)-D56 Polypropylene, Talc filled, Compounded, Elastomer, Impact modified
- Fainplast Compounds RK 115 Rigid PVC, Extrusion Lead Free
- Karina 846-10/79-IS-RG White PVC Compound
- H.C. Starck Grade K1 Crystalline Boron
- LyondellBasell Petrothene® NA340013 Low Density Polyethylene
- Taiwan Sheen Soon Sheenthane® A9030 Thermoplastic Polyurethane Elastomer
- SolVin 250SB Polyvinyl Chloride General Purpose - Rigid
- Solvay IGEPAL® CO 520 Surfactant
- DSM Biomedical PurSil® 20 Thermoplastic Silicone Polyether Polyurethane (TSPU)
- Arkema Group Rilsan® AECV T8L Nylon 12, Cable Sheathing Grade (Conditioned)
Copyright © lookpolymers.com All Rights Reserved