Malvern Minerals Nylon with Novacite® L-337 Quartz Filler
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | Malvern Minerals Company |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Malvern Minerals Nylon with Novacite® L-337 Quartz Filler.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product data demonstrates the effect of the Novacite® (untreated lamellar quartz) filler. A separate entry demonstrates the effect of treated Novakup® filler in nylon. The specific nylon used is Huels Nylon 12 L-1901, granulated natural, L-809-0001-0718.Information provided by Malvern Minerals Company.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 31.7 MPa | 4600 psi | after 16 hours in 50°C water |
| 41.4 MPa | 6000 psi | initial | |
| Elongation at Break | 3.5 % | 3.5 % | |
| Flexural Strength | 60.0 MPa | 8700 psi | after 16 hours in 50°C water |
| 68.9 MPa | 10000 psi | initial | |
| Flexural Modulus | 1.24 GPa | 180 ksi | after 16 hours in 50°C water |
| 2.14 GPa | 310 ksi | initial | |
| Izod Impact, Unnotched | 1.92 J/cm | 3.60 ft-lb/in |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 68.0 °C | 154 °F |
Users viewing this material also viewed the following:
- MV Labs ND870 Nd2(C2O4)3·xH2O Neodymium oxalate hydrate
- PolyOne Versalloy™ HC 9210-70N Thermoplastic Elastomer (TPE)
- ExxonMobil Escorene® LD-769 High EVA Compounding Resin (discontinued **)
- Covestro Desmopan® 445 Polyurethane
- Chosun Refractories CRS-A60 Blast Furnace Tap-Hole Refractory
- Chosun Refractories L15S Magnesia Carbon Bricks for Ladle Slag Line
- Chosun Refractories TCH-175Y Torpedo Castable
- 3M FV091 Soft Translucent Vinyl Label Products
Copyright © lookpolymers.com All Rights Reserved