| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Injection Molded |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | M. Holland Company MAGMA® LM213-C LLDPE
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Good Heat Seal, Good Tear Strength, Good ToughnessUses: BlendingProcessing Method: ExtrusionInformation provided by M. Holland.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.910 g/cc | 0.0329 lb/in³ | ASTM D1505 |
| Thickness | 31.8 microns | 1.25 mil | |
| Melt Flow | 1.9 g/10 min | 1.9 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | >= 600 % | >= 600 % | ASTM D882 |
| Film Elongation at Break, TD | >= 700 % | >= 700 % | ASTM D882 |
| Elmendorf Tear Strength MD | 450 g | 450 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 570 g | 570 g | ASTM D1922 |
| Dart Drop Test | >= 850 g | >= 1.87 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 42.1 MPa | 6100 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 37.2 MPa | 5400 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 103 °C | 217 °F |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 3.0 % | 3.0 % | ASTM D1003 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | <= 149 °C | <= 300 °F | |
| Zone 1 | 149 °C | 300 °F | |
| Melt Temperature | 182 - 232 °C | 360 - 450 °F | |
| Die Opening | 0.0810 - 0.254 cm | 0.0319 - 0.100 in | |
| Blow-up Ratio (BUR) | 1.5 - 3.0 | 1.5 - 3.0 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Form | Pellets |
Users viewing this material also viewed the following:
- LATI Latigloss 62 H2 G/50 PA 6, 50% Glass Fiber Reinforced, Heat Stabilized
- A. Schulman PP 2268-01 Polypropylene High Flow, Impact Copolymer Polypropylene
- Cotronics Duralco™ 4461 Electrically Resistant, Low Viscosity Epoxy Adhesive, Coating, and Sealant
- ELM® SoyGrease™ EP Premium Biodegradable Extreme Pressure Grease, NLGI Grade 2
- ExxonMobil 150 Mobilgear SHC Series
- BASF 3-Amino-1-propanol
- Aclo Accucomp Nylon 6 NY0700L
- Rogers Corporation 2929 Bondply Unreinforced, Hydrocarbon based Thin Film Adhesive System
Copyright © lookpolymers.com All Rights Reserved