LyondellBasell Lupolen® 5031 L HDPE, Injection Molding Grade
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Injection Molded |
| Manufacturer | LyondellBasell |
| Trade Name | Lupolen® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LyondellBasell Lupolen® 5031 L HDPE, Injection Molding Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Easy flow, injection molding grade for closures, aerosol pumps, spray nozzles for spray cans, small automotive parts such as the caps on lead/acid batteries, knobs, barrels for writing instruments and glue sticks, connector housings, garden chairs, etc.Data was collected by ISO methods and originally provided by BASF. The Lupolen® product line is now produced by Basell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.952 g/cc | 0.0344 lb/in³ | |
| Water Absorption | 0.010 % | 0.010 % | |
| Moisture Absorption at Equilibrium | 0.010 % | 0.010 % | |
| Linear Mold Shrinkage, Flow | 0.016 cm/cm | 0.016 in/in | |
| Linear Mold Shrinkage, Transverse | 0.012 cm/cm | 0.012 in/in | |
| Melt Flow | 8.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
8.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 26.0 MPa | 3770 psi | |
| Elongation at Break | >= 50 % | >= 50 % | |
| Elongation at Yield | 8.0 % | 8.0 % | |
| Tensile Modulus | 1.00 GPa | 145 ksi | |
| Tensile Impact Strength | 75.0 kJ/m² | 35.7 ft-lb/in² | |
| Tensile Creep Modulus, 1 hour | 440 MPa | 63800 psi | |
| Tensile Creep Modulus, 1000 hours | 290 MPa | 42100 psi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 165 µm/m-°C @Temperature 20.0 °C |
91.7 µin/in-°F @Temperature 68.0 °F |
|
| Melting Point | 131 °C | 268 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 75.0 °C | 167 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | |
| Vicat Softening Point | 74.0 °C | 165 °F | |
| Flammability, UL94 | HB @Thickness 0.400 mm |
HB @Thickness 0.0157 in |
|
| Oxygen Index | 17 % | 17 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | |
| Dielectric Constant | 2.4 @Frequency 100 Hz |
2.4 @Frequency 100 Hz |
|
| 2.4 @Frequency 1e+6 Hz |
2.4 @Frequency 1e+6 Hz |
||
| Dielectric Strength | 150 kV/mm | 3810 kV/in | |
| Dissipation Factor | 0.00020 @Frequency 100 Hz |
0.00020 @Frequency 100 Hz |
|
| 0.00020 @Frequency 1e+6 Hz |
0.00020 @Frequency 1e+6 Hz |
||
| Comparative Tracking Index | 600 V | 600 V |
Users viewing this material also viewed the following:
- Polimeros Mexicanos Rotolene® Diesel Tank Medium Density Polyethylene
- Premix Thermoplastics PREFLEX E12.5 Polyphenylene Ether (PPO/PPE)
- LyondellBasell Petrothene® NA442051 Low Density Polyethylene
- ChevronTexaco Gear Compounds EP, ISO 320
- Esstech X-969-0000 Ethoxyethyl Methacrylate, C8H14O3
- Dow LDPE 510I Low Density Polyethylene
- BASF Paliogen® Blue L 6470 Color Additive
- Addcomp ADD-VANCE® NU 559 Nucleation masterbatch, PP based
- Ascend Performance Materials Vydyne® 67R Nylon 66, Heat Stabilized, DAM
- Solvay Specialty Polymers Amodel® AF-1133 V0 Polyphthalamide (PPA) Resin, 33% Glass Reinforced, at 50% RH (di
Copyright © lookpolymers.com All Rights Reserved