Lucobit Lucofin® 7410 HFFR EBA MDH Cable Sheathing
| Category | Polymer , Thermoplastic , Ethylene Butyl Acrylate |
| Manufacturer | Lucobit AG |
| Trade Name | Lucofin® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lucobit Lucofin® 7410 HFFR EBA MDH Cable Sheathing.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Lucofin® 7410 HFFR is a thermoplastic, halogen free flame retardant and low smoke compound for the insulation and/ or sheathing of cables. This grade is based on ethylene butyl acrylate (EBA) and aluminum tri hydrate (ATH). Lucofin® 7410 HFFR combines good extrusion properties with flame retardancy.The properties of Lucofin® 7410 HFFR are in compliance with VDE 0207 part 24(HM 2/4), VDE 0207 part 23 (HJ2), BS 6724 as well as other power and telecom standards.Information provided by Lucobit AG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | ISO 1183 |
| pH | 5.9 | 5.9 | |
| Mooney Viscosity | 39 @Temperature 140 °C |
39 @Temperature 284 °F |
ML (1+4); ASTM D 792 |
| Halogen Content | <= 0.050 % | <= 0.050 % | IEC 754-1 |
| Melt Flow | 6.0 g/10 min @Load 21.6 kg, Temperature 150 °C |
6.0 g/10 min @Load 47.6 lb, Temperature 302 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 52 | 52 | ISO R 868 |
| Tensile Strength | 10.7 MPa | 1550 psi | Aged 7 days @ 110°C; IEC 60811-1-1 |
| 11.0 MPa | 1600 psi | IEC 60811-1-1 | |
| Elongation at Break | 144 % | 144 % | Cold; IEC 60811-1-4 |
| 155 % | 155 % | Aged 7 days @ 110°C; IEC 60811-1-1 | |
| 180 % | 180 % | IEC 60811-1-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Oxygen Index | 36 % | 36 % | ISO 4589-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.10e+15 ohm-cm | 1.10e+15 ohm-cm | IEC 60167 |
| 3.60e+14 ohm-cm @Temperature 70.0 °C |
3.60e+14 ohm-cm @Temperature 158 °F |
7 days water immersion; IEC 60167 | |
| Surface Resistance | 3.70e+14 ohm | 3.70e+14 ohm | IEC 60093 |
| 4.80e+14 ohm @Temperature 70.0 °C |
4.80e+14 ohm @Temperature 158 °F |
7 days water immersion; IEC 60093 | |
| Dielectric Constant | 3.7 @Frequency 50.0 Hz |
3.7 @Frequency 50.0 Hz |
IEC 60520 |
| 6.1 @Frequency 50.0 Hz, Temperature 20.0 °C |
6.1 @Frequency 50.0 Hz, Temperature 68.0 °F |
24h water immersion; IEC 60520 | |
| Dissipation Factor | 0.0263 @Frequency 50.0 Hz |
0.0263 @Frequency 50.0 Hz |
IEC 60520 |
| 0.133 @Frequency 50.0 Hz, Temperature 20.0 °C |
0.133 @Frequency 50.0 Hz, Temperature 68.0 °F |
24h water immersion; IEC 60520 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 165 - 175 °C | 329 - 347 °F |
Users viewing this material also viewed the following:
- M. Holland Company AB308LG ABS Acrylonitrile Butadiene Styrene
- Kazanorgsintez PE2NT 15-5 Linear Low Density Polyethylene
- SABIC Innovative Plastics NORYL V0150B PPE+HIPS (Asia Pacific)
- Solvay Specialty Polymers Polidan® EC/110 Polyethylene, Crosslinked (XLPE)
- Saint-Gobain Korel® K30-15 Soft Micro-cellular Polyurethane Foam
- Samsung Cheil Industries Infino® TK-2046H PCT, Glass Filled
- Formosa Plastics Formolene® 4142T Injection Molding Polypropylene
- A. Schulman POLYBATCH™ Blue 4500 Concentrate Based In Polyethylene
- Dow HDPE 25455N High Density Polyethylene
- Toyobo E2080A Thermoplastic Polyurethane Elastomer, Extrusion Grade
Copyright © lookpolymers.com All Rights Reserved