NIZHNEKAMSKNEFTEKHIM PE 4118Q (18403) Linear Low Density Polyethylene
| Category | Polymer , Thermoplastic , Polyethylene (PE) , LLDPE |
| Manufacturer | NIZHNEKAMSKNEFTEKHIM Inc |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NIZHNEKAMSKNEFTEKHIM PE 4118Q (18403) Linear Low Density Polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.916 - 0.920 g/cc | 0.0331 - 0.0332 lb/in³ | Base Resin; ASTM D1505 |
| Melt Flow | 2.6 - 3.2 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.6 - 3.2 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1283/L |
| 78 - 96 g/10 min @Load 21.6 kg, Temperature 190 °C |
78 - 96 g/10 min @Load 47.6 lb, Temperature 374 °F |
Flow@21.6kg/Flow@2.16kg ratio < 30; ASTM D1283 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | >= 50.0 MPa | >= 7250 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | >= 24.0 MPa | >= 3480 psi | ASTM D882 |
| Film Elongation at Break, MD | >= 480 % | >= 480 % | ASTM D882 |
| Film Elongation at Break, TD | >= 850 % | >= 850 % | ASTM D882 |
| Tensile Modulus | >= 0.115 GPa | >= 16.7 ksi | 2% sec, MD; ASTM D882 |
| >= 0.120 GPa | >= 17.4 ksi | 2% sec, TD; ASTM D882 | |
| Elmendorf Tear Strength, MD | >= 3.54 g/micron | >= 90.0 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | >= 13.8 g/micron | >= 350 g/mil | ASTM 1922 |
| Dart Drop Test | >= 70.0 g | >= 0.154 lb | ASTM D1709 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Gel Content (pcs./m²) | 0 | > 1mm |
| 245 | (0.2-0.5)mm | |
| 250 | > 0.2mm (totally) | |
| 5 | (0.5-1.0)mm |
Users viewing this material also viewed the following:
- Indium Corp. Indalloy 29 Bismuth Solder Alloy
- Lanxess Pocan® T 3150 XF 000000 PBT + PET, 55% Glass Fiber
- Techmer ES HiFill® PA6/6 GF43 HS L BK001 43% Glass Filled
- A. Schulman POLYFORT™ FXP 1245U UV Stable Copolymer Polypropylene
- ChevronTexaco Multifak® EP NLGI Grade 0
- ChevronTexaco URSA® SAE 10W Super Plus
- ExxonMobil 460 Mobilith SHC PM
- Hexcel® HexForce™ 5354 Aramid Fabric
- Braskem H 605 Extrusion Polypropylene
Copyright © lookpolymers.com All Rights Reserved