Lucent Polymers PPC-320 Polypropylene, Impact Modified
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Impact Modified; Molded/Extruded |
| Manufacturer | Lucent Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lucent Polymers PPC-320 Polypropylene, Impact Modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Add "U" for UV StabilizedAdd "H" for Heat StabilizedInformation provided by Lucent Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.910 g/cc | 0.910 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.016 cm/cm @Thickness 3.17 mm |
0.016 in/in @Thickness 0.125 in |
1/8" Section |
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 230 °C |
20 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 29.66 MPa | 4302 psi | ASTM D638 |
| Elongation at Break | >= 10 % | >= 10 % | ASTM D638 |
| Flexural Strength | 34.48 MPa | 5001 psi | ASTM D790 |
| Flexural Modulus | 0.68966 GPa | 100.03 ksi | ASTM D790 |
| Izod Impact, Notched | 1.50 J/cm @Thickness 3.17 mm |
2.80 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 48.89 °C | 120.0 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Multibase TPSiV™ 3010-50A Thermoplastic Silicone Vulcanizate
- Solvay Engineered Polymers SEQUEL® 2322 Engineered Polyolefin (discontinued **)
- Huntsman Araldite PZ 3907 Water-Based Adhesive/Coating
- Indium Corp. Indalloy® 151 Pb-Sn-Ag Solder Alloy
- Multibase Multi-Flex® TPE A 4710 NAT
- Wellman Wellamid® FRGS25-66-NBK3 Nylon 66, 25% Glass Sphere Reinforced, Flame Retardant
- ExxonMobil Heptene
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 2.0 PHR Zinc Stearate
- Osprey Metals 440C Stainless Steel Powder (Grade 80% - 22)
Copyright © lookpolymers.com All Rights Reserved