Lucent Polymers L6-140 Nylon 6, 15% Glass Fiber and 25% Mineral Reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled , Nylon 6, 30% Mineral Filled |
| Manufacturer | Lucent Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lucent Polymers L6-140 Nylon 6, 15% Glass Fiber and 25% Mineral Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Add "H" for Heat Stabilized Add "HU" for WeatherableTypical Properties, Dry as MoldedInformation provided by Lucent Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.48 g/cc | 1.48 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm @Thickness 3.17 mm |
0.0040 in/in @Thickness 0.125 in |
1/8" Section |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 100 MPa | 14500 psi | ASTM D638 |
| Elongation at Break | >= 1.0 % | >= 1.0 % | ASTM D638 |
| Flexural Strength | 151.72 MPa | 22005 psi | ASTM D790 |
| Flexural Modulus | 6.2069 GPa | 900.24 ksi | ASTM D790 |
| Izod Impact, Notched | 0.427 J/cm @Thickness 3.17 mm, Temperature 22.8 °C |
0.800 ft-lb/in @Thickness 0.125 in, Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 210 - 225 °C | 410 - 437 °F | ASTM D789 |
| Deflection Temperature at 1.8 MPa (264 psi) | 194.44 °C | 381.99 °F | ASTM D648 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 3413HF PC (Asia Pacific)
- Braskem BT 003 HDPE Blow Molding Polyethylene (discontinued **)
- Freudenberg Simrit V158 Fluoroelastomer Self-Lube
- Solvay TECHNYL® C 218 V33 PA6, 33% glass fiber, Eh 50
- Teknor Apex Sinvicomp SPF 3520 Polyvinyl Chloride, Flexible
- A. Schulman PP 1248-01 Polypropylene High-Flow Homopolymer Polypropylene
- ExxonMobil Nuto 100 H Series
- Ensinger TECASINT 8001 Polytetrafluoroethylene (PTFE) + Polyimide, 20% (PI)
- Ascend Performance Materials Vydyne® R533H NT Nylon 66, 33% Glass Reinforced, Conditioned
- Azoty Tarnow™ TARNOFORM 300 GB2 POM
Copyright © lookpolymers.com All Rights Reserved