- Lucent Polymers CPP-220 Polypropylene, 20% Calcium Carbonate Filled, Impact Modified
Lucent Polymers CPP-220 Polypropylene, 20% Calcium Carbonate Filled, Impact Modified
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Calcium Carbonate (CaCO3) Filler |
| Manufacturer | Lucent Polymers |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lucent Polymers CPP-220 Polypropylene, 20% Calcium Carbonate Filled, Impact Modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Melt Flow Adjustable for ApplicationAdd "U" for UV StabilizedAdd "H" for Heat StabilizedInformation provided by Lucent Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.012 cm/cm @Thickness 3.17 mm |
0.012 in/in @Thickness 0.125 in |
1/8" Section |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 24.14 MPa | 3501 psi | ASTM D638 |
| Elongation at Break | >= 10 % | >= 10 % | ASTM D638 |
| Flexural Strength | 41.38 MPa | 6002 psi | ASTM D790 |
| Flexural Modulus | 1.586 GPa | 230.1 ksi | ASTM D790 |
| Izod Impact, Notched | 0.961 J/cm @Thickness 3.17 mm |
1.80 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ASTM D648 |
Users viewing this material also viewed the following:
- PolyOne Bergamid™ A700 G20 HW UF Polyamide 66 (Nylon 66)
- Freudenberg Simrit Simriz® 486 Universal FFKT Perfluoroelastomer Compound
- Momentive Performance Materials TSE399 Translucent Adhesive Sealant, Flowable
- SABIC Innovative Plastics LNP STAT-KON CD000I PS (Asia Pacific)
- Master Bond FL901S Silver Filled, Electrically Conductive Adhesive Film
- A. Schulman POLYFLAM™ FPP 1007 Talc Filled Homopolymer Polypropylene
- Eastman Tenite 383A2R30010 Cellulose Acetate Propionate, Natural, Trsp
- Ensinger Tecapeek® XP-108 Compression Molded PEEK Compound, 20% PTFE Filled
- ExxonMobil Mobilarma 245
- Ametek P410L P/M Stainless Steel, Sintered from 6.6 g/cc Green Density
Copyright © lookpolymers.com All Rights Reserved