- Lucas-Milhaupt Silvaloy® A56T Flux Coated Rod Brazing Alloy
Lucas-Milhaupt Silvaloy® A56T Flux Coated Rod Brazing Alloy
| Category | Metal , Nonferrous Metal , Precious Metal , Silver Alloy , Solder/Braze Alloy |
| Manufacturer | Lucas-Milhaupt |
| Trade Name | Silvaloy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lucas-Milhaupt Silvaloy® A56T Flux Coated Rod Brazing Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Silvaloy A56T Flux Coated Rod has the lowest brazing temperature, best wetting, and best flow of all the cadmium free alloys. It has a slight plastic range which may be noticed during melting on some applications. Its low zinc content minimizes problems due to longer heating cycles or due to excessive heating. It is often selected for use on silver or stainless steel due to its excellent color match. Typical applications are the joining of ferrous, non-ferrous, and dissimilar metals and alloys with close joint clearances.Information provided by Lucas-Milhaupt Warwick, LLC (formerly Wolverine Joining Technologies).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 9.49 g/cc | 9.49 g/cc | |
| Density | 9.492 g/cc | 0.3429 lb/in³ | |
| Water Absorption | 15 - 35 % | 15 - 35 % |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 618.3 - 651.7 °C | 1145 - 1205 °F | |
| Solidus | 618.3 °C | 1145 °F | |
| Liquidus | 651.7 °C | 1205 °F | |
| Maximum Service Temperature, Air | 204 °C | 400 °F | continuous |
| 316 °C | 600 °F | intermittent |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Copper, Cu | 21 - 23 % | 21 - 23 % | |
| Other, total | <= 0.15 % | <= 0.15 % | |
| Silver, Ag | 55 - 57 % | 55 - 57 % | |
| Tin, Sn | 4.5 - 5.5 % | 4.5 - 5.5 % | |
| Zinc, Zn | 15 - 19 % | 15 - 19 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.0000145 ohm-cm | 0.0000145 ohm-cm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 651.7 - 760 °C | 1205 - 1400 °F | Brazing Temperature |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Boric Acid % | 25-40 | percentage of flux |
| Color | White | |
| Electrical Conductivity (% IACS) | 11.9 | |
| Potassium Bifluoride % | 10-30.0 | percentage of flux |
| Potassium Fluoride % | 5-15.0 | percentage of flux |
| Potassium Fluoroborate % | 5-20.0 | percentage of flux |
| Potassium Tetraborate % | 15-25 | percentage of flux |
Users viewing this material also viewed the following:
- PolyOne Geon™ 83510 Polyvinyl Chloride, Rigid (PVC, Rigid)
- Shakespeare WP-104 diameter 0.4 mm Weft Polyester Monofilament
- Solvay Specialty Polymers Ryton® R-4-280NA Polyphenylene Sulfide (PPS), Glass Fiber
- Shanghai Ofluorine M-1 PVDF Molding Grade
- SABIC Innovative Plastics LNP STAT-KON FX98500C PE
- Zell-Metall Engineering Plastics Zellamid 1100 OIL
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 3.0 PHR Di-Cup 40C
- Ashley Polymers Ashlene® P105 PBT Polyester
- Plaskolite West Optix® CA-1000 I Clear High Impact Acrylic Resin
- Teknor Apex APEX® 3302-65 Polyvinyl Chloride, Flexible
Copyright © lookpolymers.com All Rights Reserved