Lubrizol STAT-RITE® E-1140 Ester-Type Static Dissipative Polymer

Category	Polymer , Thermoplastic , Elastomer, TPE , Polyurethane, TP
Manufacturer	Lubrizol (former Noveon)
Trade Name	Stat-Rite®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Lubrizol STAT-RITE® E-1140 Ester-Type Static Dissipative Polymer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: Stat-Rite® E-1140 is a static dissipative thermoplastic polyurethane (TPU) alloy. Stat-Rite E-1140 utilizes the patented Stat-Rite inherently dissipative polymer (IDP) alloy system to provide clean, permanent ESD protection. Stat-Rite alloys retain uniform static dissipation properties even when injection molded or extruded.Features: Permanently static dissipativeDoes not require humidityUltra-clean: low off-gassing, low ionicsSee-through clarityNo particulatesApplications: Cleanroom soft walls, windows and doorsVacuum tubingWork surface matsAvailable in Americas, Europe, Middle East, Africa, India and AsiaInformation provided by Lubrizol.

Physical Properties	Metric	English	Comments
Specific Gravity	1.20 g/cc	1.20 g/cc	ASTM D792

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	82	82	ASTM D2240
Tensile Strength at Break	30.0 MPa	4350 psi	ASTM D412
Elongation at Break	670 %	670 %	ASTM D412
100% Modulus	0.00510 GPa	0.740 ksi	ASTM D412
300% Modulus	0.00800 GPa	1.16 ksi	ASTM D412
Tear Strength	65.0 kN/m	371 pli	ASTM D646

Electrical Properties	Metric	English	Comments
Volume Resistivity	2.00e+10 ohm-cm	2.00e+10 ohm-cm	ASTM D257
Surface Resistance	1.00e+10 ohm	1.00e+10 ohm	ASTM D257
Surface Resistivity per Square	1.10e+11 ohm	1.10e+11 ohm	ASTM D257
Static Decay	0.90 sec	0.90 sec	12% RH (+5000 V to 50 V); FTMS-101C
	0.90 sec	0.90 sec	12% RH (-5000 V to -50 V); FTMS-101C

Processing Properties	Metric	English	Comments
Drying Temperature	105 °C	221 °F	dehumidifying hopper
Dry Time	2.00 - 3.00 hour	2.00 - 3.00 hour

Descriptive Properties	Value	Comments
Color	Transparent