Lubrizol Estane® 2355-55DE Thermoplastic Polyurethane
| Category | Polymer , Thermoplastic , Polyurethane, TP |
| Manufacturer | Lubrizol (former Noveon) |
| Trade Name | ESTANE® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lubrizol Estane® 2355-55DE Thermoplastic Polyurethane.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Type: Pellethane® 2355-55DE is a thermoplastic polyurethane elastomer.Information Provided by The Lubrizol Corporation
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0090 - 0.013 cm/cm | 0.0090 - 0.013 in/in | Flow direction; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 53 | 53 | ASTM D2240 |
| Tensile Strength, Ultimate | 41.4 MPa | 6000 psi | ASTM D412 |
| Elongation at Break | 500 % | 500 % | ASTM D412 |
| 50% Modulus | 0.00930 GPa | 1.35 ksi | ASTM D412 |
| 100% Modulus | 0.0120 GPa | 1.74 ksi | ASTM D412 |
| 300% Modulus | 0.0248 GPa | 3.60 ksi | ASTM D412 |
| Flexural Modulus | 0.165 GPa | 23.9 ksi | ASTM D790 |
| Tear Strength | 114 kN/m | 650 pli | Die C; ASTM D624 |
| Taber Abrasion, mg/1000 Cycles | 60 | 60 | H-22 (coarser); ASTM D1044 |
| Compression Set | 25 % @Temperature 25.0 °C, Time 79200 sec |
25 % @Temperature 77.0 °F, Time 22.0 hour |
Method B; ASTM D395 |
| 35 % @Temperature 70.0 °C, Time 79200 sec |
35 % @Temperature 158 °F, Time 22.0 hour |
Method B; ASTM D395 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 199 - 216 °C | 390 - 421 °F | Extrusion |
| 204 - 221 °C | 399 - 430 °F | Molding | |
| Mold Temperature | 16.0 - 60.0 °C | 60.8 - 140 °F | |
| Drying Temperature | 88.0 - 104 °C | 190 - 219 °F | Air dew point <-40°C |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Elongation Set After Break (%) | 80 | ASTM D412 |
Users viewing this material also viewed the following:
- PlastiComp Complet® LCF40-PEEK Polyetheretherketone, 40% Long Carbon Fiber Reinforced
- SABIC Innovative Plastics Cycoloy® CY9640 PC+ABS (Europe-Africa-Middle East)
- SABIC Innovative Plastics Lexan® EXL1443T PC Copolymer (Europe-Africa-Middle East)
- Total Finaprene® 411x Styrene-Butadiene TPE Copolymer Compounded to 61 Shore A (discontinued **)
- LG Chemical BM662B ABS, Heat Resistance
- A. Schulman POLYBATCH™ Green 3373 Concentrate Based In Polyethylene
- Covestro Makrolon® LQ3147 Polycarbonate
- EMS-Grivory Grivory® L 16 GM nat PA12
- BASF Pluracol® P2010 Specialty Polyol
Copyright © lookpolymers.com All Rights Reserved