Lubrizol ESTANE® 58863 Ether Based Thermoplastic Polyurethane

Category	Polymer , Thermoplastic , Elastomer, TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Ether Grade
Manufacturer	Lubrizol (former Noveon)
Trade Name	ESTANE®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Lubrizol ESTANE® 58863 Ether Based Thermoplastic Polyurethane.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Features: Good Elasticity – High melt flow for easy processingUses: Extrusion – Wire and cable, general extrusionAvailable in Americas, Europe, Middle East, Africa, India and AsiaInformation provided by Lubrizol.

Physical Properties	Metric	English	Comments
Specific Gravity	1.12 g/cc	1.12 g/cc	ASTM D792
Maximum Moisture Content	0.020	0.020

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	82 - 88 @Time 5.00 sec	82 - 88 @Time 0.00139 hour	ASTM D2240
Tensile Strength	40.7 MPa	5900 psi	ASTM D412
Elongation at Break	600 %	600 %	ASTM D412
100% Modulus	0.00690 GPa	1.00 ksi	ASTM D412
300% Modulus	0.0110 GPa	1.60 ksi	ASTM D412
Flexural Modulus	0.0410 GPa	5.94 ksi	ASTM D790
Tear Strength	22.8 kN/m	130 pli	Trouser; ASTM D470
Graves Tear Strength	66.6 kN/m	380 pli	Die C; ASTM D624
Taber Abrasion, mg/1000 Cycles	4.5	4.5	CS-17, 1000g; ASTM D3389 B
Compression Set	20 % @Temperature 23.0 °C, Time 79200 sec	20 % @Temperature 73.4 °F, Time 22.0 hour
	66 % @Temperature 70.0 °C, Time 79200 sec	66 % @Temperature 158 °F, Time 22.0 hour

Thermal Properties	Metric	English	Comments
Glass Transition Temp, Tg	-50.0 °C	-58.0 °F	DSC

Processing Properties	Metric	English	Comments
Zone 1	174 °C	345 °F	Extrusion
Zone 2	180 °C	356 °F	Extrusion
Zone 3	188 °C	370 °F	Extrusion
Zone 4	194 °C	381 °F	Extrusion
Adapter Temperature	194 °C	381 °F	5, Extrusion
Die Temperature	185 °C	365 °F	Zone 2, Extrusion
	191 °C	376 °F	6, Zone 1, Extrusion
Drying Temperature	104 °C	219 °F
Dry Time	2.00 - 4.00 hour	2.00 - 4.00 hour
Dew Point	-40.0 °C	-40.0 °F