Lubrizol ESTANE® 58563 Ester Based Thermoplastic Polyurethane (European Grade)

Category	Polymer , Thermoplastic , Elastomer, TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Polyester Grade
Manufacturer	Lubrizol (former Noveon)
Trade Name	ESTANE®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Lubrizol ESTANE® 58563 Ester Based Thermoplastic Polyurethane (European Grade).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: Estane® thermoplastic polyurethanes (TPUs) include elastomeric materials that bridge the gap between flexible rubber and rigid plastics. These materials offer toughness and durability in a flexible thermoplastic elastomer system that is easy to process in a wide range of equipment. The Estane® TPU portfolio of products offers high performance polyester - and polyether - based resins and compounds in a broad range of hardnesses to meet a variety of application needs.Benefits of Estane® TPU: Outstanding Abrasion and Wear ResistanceExcellent Low Temperature FlexibilitySuperior Toughness and DurabilityEase of Processing and Manufacturing FlexibilityColorability and Paintability with no adhesion promoterApplications: Film & SheetFabric coating & melt coatingWire & CableHose, Tube & ProfileCustom moldingCustom compoundingAutomotive interior/chassis and exterior painted trimInformation provided by Noveon, Inc.

Physical Properties	Metric	English	Comments
Specific Gravity	1.44 g/cc	1.44 g/cc	DIN 53479

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	95	95	DIN 53505
Hardness, Shore D	48	48	DIN 53505
Tensile Strength, Ultimate	52.0 MPa	7540 psi	DIN 53504
Elongation at Break	560 %	560 %	DIN 53504
50% Modulus	0.00960 GPa	1.39 ksi	DIN 53504
100% Modulus	0.0101 GPa	1.46 ksi	DIN 53504
300% Modulus	0.0159 GPa	2.31 ksi	DIN 53504
Tear Strength	90.0 kN/m	514 pli	DIN 53515

Descriptive Properties	Value	Comments
BaSO4 Content	20%