Ashley Polymers Ashlene® 830L-50G Nylon 6, 50% Glass Reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 50% Glass Fiber Filled |
| Manufacturer | Ashley Polymers |
| Trade Name | Ashlene® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ashley Polymers Ashlene® 830L-50G Nylon 6, 50% Glass Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6, 50% glass reinforced resin.Data provided by the manufacturer
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.56 g/cc | 0.0564 lb/in³ | ASTM D792 |
| Water Absorption | 1.1 % | 1.1 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 221 MPa | 32100 psi | ATSM D638 |
| Elongation at Break | 1.0 % | 1.0 % | ASTM D638 |
| Elongation at Yield | 1.0 % | 1.0 % | ASTM D638 |
| Flexural Strength | 304 MPa | 44100 psi | ASTM D790 |
| Flexural Modulus | 13.8 GPa | 2000 ksi | ASTM D790 |
| Izod Impact, Notched | 1.44 J/cm | 2.70 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 216 °C | 421 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 216 °C | 421 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ASTM D648 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP LUBRICOMP DL003 PC
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 120 PHR N330 Filler
- Honeywell Aegis™ OX High Barrier Nylon (discontinued **)
- Glastic Laminates/Shapes TSF Fiberglass-Reinforced Polyester Laminate
- Haynes Multimet® alloy, 1.6 mm thick sheet, 1177°C heat treatment, rapid air cooled
- Sylvin Technologies 8940-95 Natural PVC Extrusion Compound
- Skamol Group V-1100 600 Vermiculite Insulating Slab
- UBE UBEPOL BR150L Non-Oil Extended Synthetic Rubber Vulcanizate (Cured 35 Minutes at 145°C)
- Master Bond EP21TDCS Two Component Silver Conductive Epoxy Adhesive
- Hexcel® HexPly® M56 180°C (350°F) Out-of-Autoclave Curing Matrix, M56/40%/285T2/AS4C-6K
Copyright © lookpolymers.com All Rights Reserved