Lubrizol Advanced Materials Pearlbond® DIPP-119 Thermoplastic Polyurethane
| Category | Polymer , Thermoplastic , Polyurethane, TP |
| Manufacturer | Lubrizol Advanced Materials Manufacturing S. S.L. (Former Merquinsa) |
| Trade Name | Pearlbond® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lubrizol Advanced Materials Pearlbond® DIPP-119 Thermoplastic Polyurethane.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Pearlbondâ„¢ DIPP-119 is polycaprolactone copolyester based thermoplastic polyurethane, supplied in form of translucent pellets. Featuring low melting point and excellent transparency, this product offers excellent flexibility, elasticity and easy processing. Ideally used for extrusion or compound with PVC.Applications: Pearlbondâ„¢ DIPP-119 is used mostly in extrusion applications where low melting point as well as improved adhesion over polar substrates is highly appreciated. It is ideal for PVC compounding. It is also used in solvent coating on textile substrates.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.16 g/cc | 1.16 g/cc | ISO 2781 |
| Melt Flow | 25 - 50 g/10 min @Load 5.00 kg, Temperature 190 °C |
25 - 50 g/10 min @Load 11.0 lb, Temperature 374 °F |
ISO 1133 |
| Storage Temperature | 15.0 - 25.0 °C | 59.0 - 77.0 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 70.0 | 70.0 | ISO 2781 |
| Tensile Strength at Break | 12.0 MPa | 1740 psi | ISO 527 |
| Elongation at Break | 800 % | 800 % | ISO 527 |
| 100% Modulus | 0.00200 GPa | 0.290 ksi | ISO 527 |
| 300% Modulus | 0.00300 GPa | 0.435 ksi | ISO 527 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 100 - 110 °C | 212 - 230 °F | MQSA 70 A |
| Softening Point | 90.0 - 100 °C | 194 - 212 °F | MQSA 70A |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 120 - 130 °C | 248 - 266 °F | |
| Zone 2 | 145 - 155 °C | 293 - 311 °F | |
| Zone 3 | 160 - 170 °C | 320 - 338 °F | |
| Zone 4 | 165 - 175 °C | 329 - 347 °F | |
| Die Temperature | 145 - 155 °C | 293 - 311 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Crystallization Rate | High | MQSA 12 B |
| Thermoplasticity | High | MQSA 68 A |
Users viewing this material also viewed the following:
- Americas Styrenics Styron® XL-8023VC High Impact Polystyrene (discontinued **)
- Ineos Nova S-3500MG Compact Polystyrene Microgranulates (discontinued **)
- PolyOne Geon™ Vinyl Flexible R4294Y Polyvinyl Chloride, Flexible (PVC, Flexible)
- SABIC Innovative Plastics Valox® IQ4860HR PBT (Europe-Africa-Middle East)
- Trelleborg Sealing Solutions HiMod® 911 Thermoplastic Bearing
- ThyssenKrupp PAS 550 Structural Steel for Cold Forming
- 3M Hi-Strength 94 ET Cylinder Spray Adhesive
- 3M Scotchcal™ IJ3630-20 Translucent Graphic Film
- Axiall 7055 Rigid PVC, Extrusion
- PSM Industries Pacific Sintered Metals Iron F-241-S2 Powdered Metal
Copyright © lookpolymers.com All Rights Reserved