Lubrizol Advanced Materials PEARLTHANE® 16N92 Thermoplastic Polyurethane Elastomer  (discontinued **)

Category Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Polyester Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lubrizol Advanced Materials PEARLTHANE® 16N92 Thermoplastic Polyurethane Elastomer  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PEARLTHANE® 16N92 is a polyether based TPU, supplied in form of translucent, colorless pellets, combining hardness with excellent mechanical properties and excellent hydrolysis resistance. It can be extruded and injection-molded. PEARLTHANE® 16N92 when extruded is used for making films, cables, tubing and profiles. When processed by injection molding, it can be used for making technical parts.All information provided by Merquinsa
Physical Properties Metric English Comments
Specific Gravity 1.12 g/cc
1.12 g/cc
ASTM D792
Melt Flow 10 g/10 min

@Load 21.6 kg
10 g/10 min

@Load 47.6 lb
Mechanical Properties Metric English Comments
Hardness, Shore A 92
92
ASTM D2240
Tensile Strength, Yield 40.1 MPa
5810 psi
ASTM D412
Elongation at Break 520 %
520 %
ASTM D412
100% Modulus 0.00896 GPa
1.30 ksi
ASTM D412
300% Modulus 0.0170 GPa
2.47 ksi
ASTM D412
Tear Strength 125 kN/m
715 pli
ASTM D624 (Die C)
Abrasion 25
25
loss (mm³); DIN 53.516
Compression Set 27 %

@Temperature 22.8 °C,
Time 252000 sec
27 %

@Temperature 73.0 °F,
Time 70.0 hour
ASTM D395
40 %

@Temperature 70.0 °C,
Time 86400 sec
40 %

@Temperature 158 °F,
Time 24.0 hour
ASTM D395
Thermal Properties Metric English Comments
Melting Point 182 - 193 °C
360 - 379 °F
MQSA 111
Processing Properties Metric English Comments
Feed Temperature 193 °C
380 °F
Nozzle Temperature 199 °C
390 °F
Zone 1 204 °C
400 °F
Compression Zone
Zone 2 210 °C
410 °F
Metering Zone
Mold Temperature 35.0 °C
95.0 °F
Moisture Content <= 0.10 %
<= 0.10 %
MQSA 44
Injection Pressure 11.0 MPa
1600 psi
Hold Pressure 4.83 MPa

@Time 15.0 sec
700 psi

@Time 0.00417 hour
Cycle Time - Injection 3.7 sec
3.7 sec
Cycle Time - Cooling 38 sec
38 sec
Screw Speed 130 rpm
130 rpm