- Lotte Chemical Titan TITANLENE® LDF265YZ Low density polyethylene
Lotte Chemical Titan TITANLENE® LDF265YZ Low density polyethylene
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Extrusion Grade |
| Manufacturer | Lotte Chemical Titan Holding Sdn. Bhd. (Former Titan Chemicals) |
| Trade Name | TITANLENE® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lotte Chemical Titan TITANLENE® LDF265YZ Low density polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LDF265YZ is a low density polyethylene resin for film extrusion. LDF265YZ has no slip and anti-block additives. LDF265YZ meets the U.S. Food and Drug Administration (FDA) criteria for food contact use as specified in 21 CFR 177.1520 (c) 2.1 & (c) 2.2.Applications: Heavy duty sacks Shrink film Construction filmAdditives: BarefootAdvantages: Excellent mechanical properties Good process abilityInformation provided by Titan Chemicals
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Base Resin Density | 0.922 g/cc | 0.0333 lb/in³ | ASTM D1505 |
| Thickness | 150 microns | 5.91 mil | extruded at 1.5:1 BUR |
| Base Resin Melt Index | 0.33 g/10 min | 0.33 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 250 % | 250 % | ASTM D882 |
| Film Elongation at Break, TD | 660 % | 660 % | ASTM D882 |
| Dart Drop | 11.0 g/micron | 279 g/mil | ASTM D1709 |
| Film Tensile Strength at Break, MD | 78.5 MPa | 11400 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 53.9 MPa | 7820 psi | ASTM D882 |
| 1% Secant Modulus, MD | 1275.5 MPa | 185000 psi | ASTM D882 |
| 1% Secant Modulus, TD | 1179.0 MPa | 171000 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 97.0 °C | 207 °F | resin; ASTM D1525 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 160 - 190 °C | 320 - 374 °F | |
| Blow-up Ratio (BUR) | 1.5 | 1.5 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Trouser tear, MD g/micron | 9 | ASTM D1938 |
| Trouser tear, TD g/micron | 8.5 | ASTM D1938 |
Users viewing this material also viewed the following:
- Albis Plastics Polyamide 6/66 PA 152 GF30/02 BK8-1114 Black 30% Glass Fiber (discontinued **)
- Kazanorgsintez PC-075A Polycarbonate
- Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 4.8 mm thick sheet
- Lubriplate SPO-222 Petroleum-Based Gear, Bearing, & Recirculating Oil
- KaMin Polyfil® 70 Kaolin Clay - Calcined
- Solvay Specialty Polymers Amodel® A-1133 L WH 015 Polyphthalamide (PPA), 33% Glass Fiber
- A. Schulman POLYBLAK™ 4479-01 Black Color Concentrate, 50% Carbon Black Based In LLDPE
- Loctite® 262 Medium to High Strength Threadlocker
- 3M Scotchkote™ EA5WB WB Epoxy Coating
- Alliance Polymers Zythane™ 7085AU Thermoplastic Polyurethane Elastomer
Copyright © lookpolymers.com All Rights Reserved