- Lotte Chemical Titan TITANLENE® LDF201FG Low density polyethylene
Lotte Chemical Titan TITANLENE® LDF201FG Low density polyethylene
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Extrusion Grade |
| Manufacturer | Lotte Chemical Titan Holding Sdn. Bhd. (Former Titan Chemicals) |
| Trade Name | TITANLENE® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lotte Chemical Titan TITANLENE® LDF201FG Low density polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LDF201FG is a low density polyethylene resin for film extrusion. LDF201FG has low slip and anti-block additives. LDF201FG meets the U.S. Food and Drug Administration (FDA) criteria for food contact use as specified in 21 CFR 177.1520 (c) 2.1 & (c) 2.2.Applications: Produce film T-shirt carrier bags Display packagingAdditives: Low slip AntiblockAdvantages: Good optical Good mechanical propertiesInformation provided by Titan Chemicals
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Base Resin Density | 0.922 g/cc | 0.0333 lb/in³ | ASTM D1505 |
| Thickness | 30.0 microns | 1.18 mil | extruded at 2.5:1 BUR |
| Base Resin Melt Index | 3.0 g/10 min | 3.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 310 % | 310 % | ASTM D882 |
| Film Elongation at Break, TD | 580 % | 580 % | ASTM D882 |
| Elmendorf Tear Strength, MD | 6.00 g/micron | 152 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 4.00 g/micron | 102 g/mil | ASTM D1922 |
| Dart Drop | 2.00 g/micron | 50.8 g/mil | ASTM D1709 |
| Film Tensile Strength at Break, MD | 26.5 MPa | 3840 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 21.6 MPa | 3130 psi | ASTM D882 |
| 1% Secant Modulus, MD | 205.94 MPa | 29869 psi | ASTM D882 |
| 1% Secant Modulus, TD | 225.56 MPa | 32714 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 95.0 °C | 203 °F | resin; ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 7.0 % | 7.0 % | ASTM D1003 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 160 - 190 °C | 320 - 374 °F | |
| Blow-up Ratio (BUR) | 2.5 | 2.5 |
Users viewing this material also viewed the following:
- Quadrant EPP Nylatron® LIG Oil Filled Cast 6 Nylon (ASTM Product Data Sheet)
- Special Metals DURANICKEL® 301 (UNS N03301) Annealed Strip
- Techmer ES HiFill® PA6/6 GF50 X BK 50% Glass Filled
- Teknor Apex Beetle® A82 Nylon 66, Non-Halogenated
- A. Schulman PP 828-01 Polypropylene Molding Grade Impact Polypropylene
- Universal Wire Works ER209 Stainless Steel Bare Wire
- CP-Polymer-Technik Wellamid® 6000/58 HWUVCP Nylon 6, Impact Modified Until -40°C, UV Stabilized, Heat Stabilized, Dry
- 3M Scotch-Weld™ Medium Instant Wood Adhesives and Surface Activator
Copyright © lookpolymers.com All Rights Reserved