Lotte Chemical Titan TITANEX® LF2024 Linear low density polyethylene resin (discontinued **)

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Lotte Chemical Titan TITANEX® LF2024 Linear low density polyethylene resin (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LF2024 is a pelleted linear low density polyethylene resin formulated with antioxidant. This product is used for blown and cast film extrusion which offers outstanding toughness, extrudability and draw down ability.Applications: Blend, liners, stretch film, cast film, diaper film.Advantages: Outstanding toughness, high tensile strength and good puncture resistance.Information provided by Titan Chemicals

Physical Properties	Metric	English	Comments
Base Resin Density	0.920 g/cc	0.0332 lb/in³	ASTM D1505
Thickness	25.0 microns	0.984 mil	extruded at 2:1 BUR
Base Resin Melt Index	2.4 g/10 min	2.4 g/10 min	ASTM D1238

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	500 %	500 %	ASTM D882
Film Elongation at Break, TD	700 %	700 %	ASTM D882
Elmendorf Tear Strength, MD	7.00 g/micron	178 g/mil	ASTM D1922
Elmendorf Tear Strength, TD	17.0 g/micron	432 g/mil	ASTM D1922
Dart Drop	3.50 g/micron	88.9 g/mil	ASTM D1709
Film Tensile Strength at Break, MD	34.3 MPa	4970 psi	ASTM D882
Film Tensile Strength at Break, TD	24.5 MPa	3550 psi	ASTM D882
1% Secant Modulus, MD	166.7 MPa	24180 psi	ASTM D882
1% Secant Modulus, TD	196.14 MPa	28447 psi	ASTM D882

Optical Properties	Metric	English	Comments
Haze	13 %	13 %	ASTM D1003
Gloss	30 %	30 %	45°; ASTM D2457

Processing Properties	Metric	English	Comments
Melt Temperature	160 - 200 °C	320 - 392 °F	Blown film
	200 - 280 °C	392 - 536 °F	Cast film
Blow-up Ratio (BUR)	2.0 - 3.0	2.0 - 3.0	Blown film