Lotte Chemical Titan TITANCEED® mL2764 Linear low density polyethylene resin (discontinued **)

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Lotte Chemical Titan TITANCEED® mL2764 Linear low density polyethylene resin (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Titanceed® mL2764 is a pelleted metallocene linear low density polyethylene resin formulated with antioxidant. Films made from Titanceed® mL2764 have outstanding tensile properties, impact strength and puncture toughness. These superior properties along with excellent draw ability makes this a very versatile resin for both monolayer and multilayer stretch film.Applications: Cast film, and stretch film.Advantages: Superior strength and excellent draw ability.Information provided by Titan Chemicals

Physical Properties	Metric	English	Comments
Base Resin Density	0.918 g/cc	0.0332 lb/in³	ASTM D1505
Thickness	20.0 microns	0.787 mil	extruded at 750ft/min take off speed and melt temperature of 274-302°C
Base Resin Melt Index	2.7 g/10 min	2.7 g/10 min	I<sub>2</sub>; ASTM D1238

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	470 %	470 %	ASTM D882
Film Elongation at Break, TD	720 %	720 %	ASTM D882
Elmendorf Tear Strength, MD	9.00 g/micron	229 g/mil	ASTM D1922
Elmendorf Tear Strength, TD	21.0 g/micron	533 g/mil	ASTM D1922
Dart Drop	8.50 g/micron	216 g/mil	ASTM D1709A
Film Tensile Strength at Break, MD	73.5 MPa	10700 psi	ASTM D882
Film Tensile Strength at Break, TD	50.0 MPa	7250 psi	ASTM D882
1% Secant Modulus, MD	117.68 MPa	17068 psi	ASTM D882
1% Secant Modulus, TD	137.30 MPa	19913 psi	ASTM D882

Optical Properties	Metric	English	Comments
Haze	1.8 %	1.8 %	ASTM D1003
Gloss	91 %	91 %	45°; ASTM D2457

Processing Properties	Metric	English	Comments
Melt Temperature	250 - 310 °C	482 - 590 °F