- Lord Adhesives Thermosetâ„¢ MD-130 Electrically Insulating Die-Attach Adhesive
Lord Adhesives Thermosetâ„¢ MD-130 Electrically Insulating Die-Attach Adhesive
| Category | Polymer , Adhesive |
| Manufacturer | Lord Adhesives |
| Trade Name | Thermoset™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lord Adhesives Thermosetâ„¢ MD-130 Electrically Insulating Die-Attach Adhesive.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Lord MD-130 is a microelectronic grade, die-attach adhesive system for use in applications where electrical conductivity is not required. This system offers long, room temperature stability, fast cure at temperatures down to 100°C, and high die-shear strengths.All information provided by Lord.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.49 g/cc @Temperature 25.0 °C |
1.49 g/cc @Temperature 77.0 °F |
|
| Water Absorption | 0.050 % | 0.050 % | |
| Viscosity | 60000 cP | 60000 cP |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 88 | 88 | |
| Tensile Strength, Yield | 56.5 MPa | 8200 psi | |
| Elongation at Yield | 1.7 % | 1.7 % |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.418 W/m-K | 2.90 BTU-in/hr-ft²-°F | |
| Maximum Service Temperature, Air | 130 °C | 266 °F | |
| Minimum Service Temperature, Air | -55.0 °C | -67.0 °F | |
| Glass Transition Temp, Tg | 140 °C | 284 °F | Mettler DSC30 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 4.2 @Frequency 1000 Hz, Temperature 25.0 °C |
4.2 @Frequency 1000 Hz, Temperature 77.0 °F |
ASTM D150 |
| Dissipation Factor | 0.0080 @Frequency 1000 Hz, Temperature 25.0 °C |
0.0080 @Frequency 1000 Hz, Temperature 77.0 °F |
ASTM D150 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 4.00 min @Temperature 150 °C |
0.0667 hour @Temperature 302 °F |
Hot Plate |
| 8.00 min @Temperature 150 °C |
0.133 hour @Temperature 302 °F |
Oven | |
| 16.0 min @Temperature 135 °C |
0.267 hour @Temperature 275 °F |
Oven | |
| 20.0 min @Temperature 135 °C |
0.333 hour @Temperature 275 °F |
Hot Plate | |
| 34.0 min @Temperature 120 °C |
0.567 hour @Temperature 248 °F |
Hot Plate | |
| 48.0 min @Temperature 120 °C |
0.800 hour @Temperature 248 °F |
Oven | |
| 68.0 min @Temperature 100 °C |
1.13 hour @Temperature 212 °F |
Hot Plate | |
| 148 min @Temperature 100 °C |
2.47 hour @Temperature 212 °F |
Oven | |
| Gel Time | 1.00 min @Temperature 150 °C |
1.00 min @Temperature 302 °F |
Hot Plate |
| 2.00 min @Temperature 150 °C |
2.00 min @Temperature 302 °F |
Oven | |
| 4.00 min @Temperature 135 °C |
4.00 min @Temperature 275 °F |
Oven | |
| 5.00 min @Temperature 135 °C |
5.00 min @Temperature 275 °F |
Hot Plate | |
| 8.00 min @Temperature 120 °C |
8.00 min @Temperature 248 °F |
Hot Plate | |
| 12.0 min @Temperature 120 °C |
12.0 min @Temperature 248 °F |
Oven | |
| 17.0 min @Temperature 100 °C |
17.0 min @Temperature 212 °F |
Hot Plate | |
| 37.0 min @Temperature 100 °C |
37.0 min @Temperature 212 °F |
Oven | |
| Shelf Life | 6.00 Month @Temperature 25.0 °C |
6.00 Month @Temperature 77.0 °F |
|
| 12.0 Month @Temperature 4.00 °C |
12.0 Month @Temperature 39.2 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Black |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 66 GF 30 FRA 5 Polyamide 66, 30% Glass Fiber, Halogen Flame Retardant
- Pau Tai Unistab BT-11 Organotin Stabilizer Butyl/Octyl Carboxylate Tin
- Huntsman AVALON® 65 DEU Thermoplastic Polyurethane
- SABIC Innovative Plastics LNP THERMOCOMP ZFM62P PPE+PS
- SABIC Innovative Plastics NORYL NH6010B PPE+HIPS (Asia Pacific)
- A. Schulman POLYTROPE™ TPP 608 Olefinic Elastomer
- ELM® EnviroLift™ Biobased Elevator Hydraulic Oil
- Eurostar Staramide RB004 PA66, 20% Glass Bead Filled, Injection Molded
- Bulk Molding Compounds BMC A50-XHS-U Bulk molding compound
- Arkema Group Oroglas® V 920 Acrylic, Injection Molding Grade (discontinued **)
Copyright © lookpolymers.com All Rights Reserved