- Lehmann & Voss LUVOCOM® 80-8284 Polyacetal-copolymer, with carbon fiber
Lehmann & Voss LUVOCOM® 80-8284 Polyacetal-copolymer, with carbon fiber
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Carbon Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 80-8284 Polyacetal-copolymer, with carbon fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Electrically conductive, suitable for continuous discharging of statically generated electricity.No change of electric potential at bearings in case of separation of charge caused by transport and guiding of paper and foil.Transporting equipment for electrically sensible goods.No mass temperature above 215°C! Ventilation of machinery is recommended.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.44 g/cc | 1.44 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0090 - 0.014 cm/cm | 0.0090 - 0.014 in/in | |
| Melt Flow | 28.8 g/10 min @Load 5.00 kg, Temperature 190 °C |
28.8 g/10 min @Load 11.0 lb, Temperature 374 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 85.0 MPa | 12300 psi | |
| Elongation at Yield | 3.0 % | 3.0 % | |
| 4.3 % | 4.3 % | flexural | |
| Modulus of Elasticity | 8.00 GPa | 1160 ksi | |
| Flexural Strength | 115 MPa | 16700 psi | |
| Flexural Modulus | 6.00 GPa | 870 ksi | |
| Charpy Impact Unnotched | 3.30 J/cm² | 15.7 ft-lb/in² | flatwise; ISO 179 1fU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 100 °C | 212 °F | |
| 120 °C | 248 °F | short term | |
| Flammability, UL94 | HB | HB | not recognized by UL |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 1.00e+8 ohm | <= 1.00e+8 ohm | |
| Insulation Resistance | <= 1.00e+8 ohm | <= 1.00e+8 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 200 °C | 392 °F | mass temp |
| Nozzle Temperature | 175 - 200 °C | 347 - 392 °F | |
| Zone 1 | 175 - 190 °C | 347 - 374 °F | |
| Zone 2 | 185 - 205 °C | 365 - 401 °F | |
| Zone 3 | 180 - 200 °C | 356 - 392 °F | |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | |
| Drying Temperature | 75.0 °C @Time 7200 - 28800 sec |
167 °F @Time 2.00 - 8.00 hour |
Dehumidifying dryer |
| 120 °C @Time 7200 - 14400 sec |
248 °F @Time 2.00 - 4.00 hour |
Air-Circulation Dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | black |
Users viewing this material also viewed the following:
- Nye Lubricants UniFlor 8731 (UF) Synthetic Oil
- NCMT NanoPAC™ S205 High Performance Polypropylene Nanocomposite
- Covestro Apec® DP9-9354 High-Heat Polycarbonate, Flame-Retardant (discontinued **)
- Karina 18/482-FC-LMP (SDB) Gray Color Concentrate for PVC
- A. Schulman POLYFORT™ FPP 3459 Glass Filled Impact Copolymer
- Polyram PlusTek PD120BK11 Nylon 12 for Extrusion, UV Stabilized
- Polyram PlusTek RA102 Nylon 6.6, General Purpose
- Cheng Yu Plastic NG1300S Nylon 66, 30% Glass Fiber Reinforced
- Covestro Desmopan® DP 3059D Polyurethane
- Arlon 0.010" (0.254 mm) Flexible Heater Silicone with Fiberglass Substrate (49586R010)
Copyright © lookpolymers.com All Rights Reserved