Lehmann & Voss LUVOCOM® 50/CF/15/TF/15/SI/2/BK-HB Polycarbonate, with carbon fiber, PTFE, lubricant modified
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Carbon Fiber Reinforced |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 50/CF/15/TF/15/SI/2/BK-HB Polycarbonate, with carbon fiber, PTFE, lubricant modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.High-strength and high-stiff parts; low coefficient of expansion.Electrically conductive, suitable for continuous discharging of statically generated electricity.Improved friction and wear behaviour. Emergency running property.High dimensionally stable precision parts, even at elevated temperatures and narrow tolerance range.Body and duty parts in office equipment, gear wheels, grippers.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.34 g/cc | 1.34 g/cc | ISO 1183 |
| Water Absorption | <= 0.20 % | <= 0.20 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 105 MPa | 15200 psi | |
| Elongation at Yield | 2.2 % | 2.2 % | |
| 2.8 % | 2.8 % | flexural | |
| Modulus of Elasticity | 10.0 GPa | 1450 ksi | |
| Flexural Strength | 150 MPa | 21800 psi | |
| Flexural Modulus | 8.50 GPa | 1230 ksi | |
| Charpy Impact Unnotched | 2.50 J/cm² | 11.9 ft-lb/in² | flatwise; ISO 179 1fU |
| Coefficient of Friction, Dynamic | 0.15 | 0.15 | |
| Coefficient of Friction, Static | 0.14 | 0.14 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 30.0 µm/m-°C | 16.7 µin/in-°F | DIN 53752 |
| Thermal Conductivity | 0.450 W/m-K | 3.12 BTU-in/hr-ft²-°F | DIN 52612 |
| Maximum Service Temperature, Air | 130 °C | 266 °F | |
| 150 °C | 302 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C | 293 °F | |
| Vicat Softening Point | 160 °C | 320 °F | DIN ISO 306 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 1e+05 | <= 1e+05 | |
| Insulation Resistance | <= 100000 ohm | <= 100000 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 295 °C | 563 °F | mass temp |
| Nozzle Temperature | 290 - 310 °C | 554 - 590 °F | |
| Zone 1 | 280 - 300 °C | 536 - 572 °F | |
| Zone 2 | 290 - 310 °C | 554 - 590 °F | |
| Zone 3 | 300 - 320 °C | 572 - 608 °F | |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | |
| Drying Temperature | 120 °C @Time 14400 - 21600 sec |
248 °F @Time 4.00 - 6.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | black |
Users viewing this material also viewed the following:
- Quadrant EPP Nylatron® GS PA 6 + MoS2, extruded (ISO Data)
- Indium Corp. Indalloy 240 Bismuth-Lead-Tin Solder Alloy
- A. Schulman POLYFORT™ FPP 1239H Glass Filled Chemically Coupled Homopolymer Polypropylene
- Cosmic Plastics ID-50 Dacron Filled Ortho Diallyl Phthalate Molding Compound
- Plenco 4301 Phenolic, Granular, Compression Molded
- Westlake Plastics HIPS High Impact Polystyrene
- Hexcel® HexWeb® CR III 1/8-5052-.0007 Corrosion Resistant Specification Grade Aluminum Honeycomb
- CoorsTek FG-995 Alumina (nom. 98.5% Al2O3)
- Protective Coating PC-Metal™ Epoxy Putty
- Adell AH-18 Nylon 66, 40% Mineral Filled
Copyright © lookpolymers.com All Rights Reserved