Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

China-Yixing Longly Refractories ASM-120 Cordierite-Mullite

Category Ceramic , Oxide , Aluminum Oxide , Magnesium Oxide , Silicon Oxide
Manufacturer China-Yixing Longly Refractories Co. Ltd
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF China-Yixing Longly Refractories ASM-120 Cordierite-Mullite.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Featured mullite, cordierite as the main raw material, the use of advanced production technology, professionally manufacturing the kiln furniture of ceramic and powder metallurgy with load bearing board, shelf, seggar, slides, plate, pillars such as high-grade kiln tools. Refractoriness higher than its cordierite, thermal stability is better than corundum mullite material. Coefficient of thermal expansion of small, good thermal shock resistance and long service life, not sudden fracture; No oxidation in the process of use, no chipping, and less pollution ceramics.Mullite - cordierite kiln furniture is better material in 1300°C following firing ceramics. In the firing of ceramics, sanitary ceramics, furnishings ceramics, mosaic glaze, western-style brick, square brick, split bricks and glass-ceramics have had excellent results. Can be used for the tunnel kiln, shuttle kiln, belt kiln putting furnace and low-temperature-fired glaze or burn, the powder metallurgy heat treatment.Application: The kiln furniture of ceramic and powder metallurgy with load bearing board, shelf, seggar, plate such as high-grade kiln tools.Information Provided by China Yixing Longly Refractories Co. Ltd
Physical Properties Metric English Comments
Bulk Density >= 1.90 g/cc
>= 0.0686 lb/in³
Porosity <= 23 %
<= 23 %
Apparent
Mechanical Properties Metric English Comments
Flexural Strength >= 18.0 MPa
>= 2610 psi
high temp bending
>= 50.0 MPa
>= 7250 psi
cold bending
Compressive Strength >= 35.0 MPa
>= 5080 psi
Ambient
Thermal Properties Metric English Comments
CTE, linear 4.20 µm/m-°C
2.33 µin/in-°F
Volumetric thermal expansion
Thermal Conductivity 1.60 W/m-K
11.1 BTU-in/hr-ft²-°F
Maximum Service Temperature, Air >= 1250 °C
>= 2280 °F
Component Elements Properties Metric English Comments
Al2O3 >= 36 %
>= 36 %
MgO >= 7.0 %
>= 7.0 %
SiO2 <= 52 %
<= 52 %
Descriptive Properties Value Comments
Refractoriness (°C) >1200
Under load temperature, 0.2 MPa, 0.6%
Thermal Shock Resistance Times 30
1100°C water cooling