Lehmann & Voss LUVOCOM® 1105-8234 PEEK, with carbon fiber, PTFE, lubricant modified
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Carbon Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1105-8234 PEEK, with carbon fiber, PTFE, lubricant modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Improved friction and wear behaviour. Emergency running property.Strong, stiff parts.Dynamic stressed parts at high movement velocity.Chemical and hydrolysis resistance parts, non flammable.Bearings, sleeves, control disks, gear wheels, pump impellers, gear parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.42 g/cc | 1.42 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | |
| Melt Flow | 14.2 g/10 min @Load 10.0 kg, Temperature 380 °C |
14.2 g/10 min @Load 22.0 lb, Temperature 716 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 195 MPa | 28300 psi | |
| Elongation at Yield | 1.5 % | 1.5 % | |
| 2.0 % | 2.0 % | flexural | |
| Modulus of Elasticity | 18.0 GPa | 2610 ksi | |
| Flexural Strength | 270 MPa | 39200 psi | |
| Flexural Modulus | 15.0 GPa | 2180 ksi | |
| Charpy Impact Unnotched | 3.50 J/cm² | 16.7 ft-lb/in² | edgewise; ISO 179 1eU |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179 1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 250 °C | 482 °F | |
| 280 °C | 536 °F | short term | |
| Flammability, UL94 | V-0 | V-0 | not recognized by UL |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 1e+05 | <= 1e+05 | |
| Insulation Resistance | <= 100000 ohm | <= 100000 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 390 °C | 734 °F | mass temp |
| Nozzle Temperature | 360 - 380 °C | 680 - 716 °F | |
| Zone 1 | 360 - 370 °C | 680 - 698 °F | |
| Zone 2 | 380 - 390 °C | 716 - 734 °F | |
| Zone 3 | 390 - 400 °C | 734 - 752 °F | |
| Mold Temperature | 170 - 200 °C | 338 - 392 °F | |
| Drying Temperature | 120 °C @Time 21600 - 28800 sec |
248 °F @Time 6.00 - 8.00 hour |
or |
| 150 °C @Time 10800 - 21600 sec |
302 °F @Time 3.00 - 6.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (black) |
Users viewing this material also viewed the following:
- MV Labs LI890 LiOH.H2O Lithium hydroxide monohydrate
- MV Labs LU300 Lu2(CO3)3·xH2O Lutetium carbonate hydrate
- Nye Lubricants 701 (NG) Synthetic Oil
- MV Labs SC200 ScBr3·xH2O Scandium bromide hydrate
- Parker Chomerics THERM-A-FORM 1642 Cure-in-Place Potting and Underfill Material
- Custom Resins Duratel™ MF3 Acetal Copolymer (discontinued **)
- Techmer ES Electrablend® ABS CF20 BK 20% Carbon Filled
- DuPont Performance Polymers VESPEL TP-8792 Polyimide
- CLAL-MSX NICLAFOR® 1000 TH1 Quenched/Precipitation Heat Treated, Rolled Copper Alloy
- Ashley Polymers Ashlene® 527 Nylon 66
Copyright © lookpolymers.com All Rights Reserved