- Lanxess Pocan® DP 7102 000000 PBT, 30% Mineral (discontinued **)
Lanxess Pocan® DP 7102 000000 PBT, 30% Mineral (discontinued **)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Mineral Filled |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Pocan® DP 7102 000000 PBT, 30% Mineral
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PBT, 30% mineral, injection molding, LDS
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.565 g/cc | 0.05654 lb/in³ | ISO 1183 |
| Viscosity Test | 64 cm³/g | 64 cm³/g | Viscosity number; ISO 307, 1157, 1628 |
| Melt Flow | 19 g/10 min @Load 2.16 kg, Temperature 260 °C |
19 g/10 min @Load 4.76 lb, Temperature 500 °F |
Estimated using room temperature density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 55.0 MPa | 7980 psi | ISO 527-1/-2 |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527-1/-2 |
| Tensile Modulus | 5.60 GPa | 812 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | 3.50 J/cm² @Temperature -30.0 °C |
16.7 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 3.50 J/cm² @Temperature 23.0 °C |
16.7 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 60.0 µm/m-°C | 33.3 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C | 50.0 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C | 383 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C | 239 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB | HB | IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.5 @Frequency 1.00e+6 Hz |
3.5 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.7 @Frequency 100 Hz |
3.7 @Frequency 100 Hz |
IEC 60250 | |
| Dissipation Factor | 0.0032 @Frequency 100 Hz |
0.0032 @Frequency 100 Hz |
IEC 60250 |
| 0.0149 @Frequency 1.00e+6 Hz |
0.0149 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 °C | 500 °F | Injection Molding; ISO 294 |
| Mold Temperature | 80.0 °C | 176 °F | Injection Molding; ISO 10724 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Release agent | |
| Form | Pellets | |
| ISO Shortname | ISO 7792-1-PBT,GHMR,09-060,MD30 | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- Nye Lubricants UniFlor 8980 (499) (UF) Synthetic Oil
- Lord Adhesives 3170 Two-component, high cold strength, cryogenic application Epoxy Adhesive
- Spartech E65070 General Purpose PVC
- SABIC Innovative Plastics NORYL GTX GTX810 PPE+PS+PA
- Chase Plastics CP Pryme® N120GL (COND, 50% RH) Nylon 6, 20% Glass Fiber Reinforced, Internally Lubricated
- Daikin POLYFLON FA-500 MPA, White Powder
- ExxonMobil LDPE LD 654 Low Density Polyethylene Resin (European Grade)
- Braskem BS002HS HDPE Blow Molding Polyethylene Copolymer
- Asahi Kasei Tenac® LA543 Homopolymer Acetal Resin
- 3M Dyneon™ ET 6210AZ Fluoroplastic Agglomerate
Copyright © lookpolymers.com All Rights Reserved